Magnetic tape, magnetic tape cartridge, and magnetic tape apparatus

ABSTRACT

A magnetic tape in which a minimum value of TDStens among five TDStens measured respectively at a temperature of 16° C. and a relative humidity of 20%, a temperature of 16° C. and a relative humidity of 80%, a temperature of 26° C. and a relative humidity of 80%, a temperature of 32° C. and a relative humidity of 20% and a temperature of 32° C. and a relative humidity of 55% is 1.43 μm/N or more, a ratio of a change of TDStens to a change of a relative humidity obtained from the five TDStens is 0.005 μm/N/% or less, and a ratio of a change of TDStens to a change of a temperature obtained from the five TDStens is 0.020 μm/N/° C. or less.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority under 35 U.S.C 119 to Japanese Patent Application No. 2019-236353 filed on Dec. 26, 2019. The above application is hereby expressly incorporated by reference, in its entirety, into the present application.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates to a magnetic tape, a magnetic tape cartridge, and a magnetic tape apparatus.

2. Description of the Related Art

There are tape-shaped and disk-shaped magnetic recording medium, and the tape-shaped magnetic recording medium, that is, a magnetic tape are mainly used for data storage applications such as data backup and archive (for example, refer to JP6590102B).

SUMMARY OF THE INVENTION

Recording of data on a magnetic tape is usually performed by running the magnetic tape in a magnetic tape apparatus (usually called “drive”) and recording the data on a data band by making a magnetic head follow the data band of the magnetic tape. As a result, a data track is formed in the data band. In addition, in a case where recorded data are reproduced, the data recorded on the data band is read by running the magnetic tape in the magnetic tape apparatus and by making the magnetic head follow the data band of the magnetic tape.

In order to increase the accuracy with which the magnetic head following the data band of the magnetic tape in the recording and/or reproduction as described above, a system (hereinafter, it is described as a “servo system”.) for performing head tracking using a servo signal has been put into practical use.

Further, dimension information in the width direction of the running magnetic tape is acquired using the servo signal, and a tension applied in the longitudinal direction of the magnetic tape is adjusted according to the acquired dimension information, thereby controlling the dimension in the width direction of the magnetic tape (refer to, for example, paragraph [0171] in JP6590102B). In a case where the magnetic head for recording or reproducing data is shifted from a target track position by the width deformation of the magnetic tape during recording or reproducing, a phenomenon such as overwriting of recorded data, defective reproduction, or the like occurs. The present inventors believe that the above-described tension adjustment is an effective means for suppressing the occurrence of such a phenomenon.

In view of the above, an object according to one aspect of the present invention is to provide the magnetic tape in which recording and/or reproduction can be performed satisfactorily by controlling the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape.

One aspect of the present invention relates to a magnetic tape comprising:

-   -   a non-magnetic support and a magnetic layer containing a         ferromagnetic powder, in which     -   the magnetic layer has a plurality of servo bands, and a region         sandwiched between two adjacent servo bands is called a data         band,     -   among five TDStens measured respectively in the following five         environments;         -   a temperature of 16° C. and a relative humidity of 20%,         -   a temperature of 16° C. and a relative humidity of 80%,         -   a temperature of 26° C. and a relative humidity of 80%,         -   a temperature of 32° C. and a relative humidity of 20%, and         -   a temperature of 32° C. and a relative humidity of 55%     -   a minimum value of the TDStens is 1.43 μm/N or more,     -   where the TDStens is a ratio of a change of a servo band         interval to a change of a tension obtained from a plurality of         servo band intervals measured by respectively applying a         plurality of different tensions in a longitudinal direction of a         magnetic tape as a value based on a magnetic tape with ½ inch         width and four total data bands,     -   a ratio of a change of the TDStens to a change of the relative         humidity, which is obtained from the five TDStens, is 0.005         μm/N/% or less, and     -   a ratio of a change of the TDStens to a change of the         temperature, which is obtained from the five TDStens, is 0.020         μm/N/° C. or less.

In one aspect, the magnetic tape can have a thickness of 5.6 μm or less.

In one aspect, the magnetic tape can have a thickness of 5.3 μm or less.

In one aspect, the minimum value of the TDStens can be 1.43 μm/N or more and 3.00 μm/N or less.

In one aspect, the magnetic tape can have a non-magnetic layer containing a non-magnetic powder, which is provided between the non-magnetic support and the magnetic layer.

In one aspect, the magnetic tape can have a back coating layer containing a non-magnetic powder on a surface side of the non-magnetic support opposite to a surface side having the magnetic layer.

In one aspect, the non-magnetic support can be an aromatic polyester support.

In one aspect, the aromatic polyester support can be a polyethylene terephthalate support.

In one aspect, the aromatic polyester support can be a polyethylene naphthalate support.

One aspect of the present invention relates to a magnetic tape cartridge including the magnetic tape.

One aspect of the present invention relates to a magnetic tape apparatus including the magnetic tape cartridge.

According to one aspect of the present invention, the magnetic tape in which recording and/or reproduction can be performed satisfactorily by controlling the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape can be provided. In addition, according to one aspect of the present invention, it is possible to provide the magnetic tape cartridge including the magnetic tape, and the magnetic tape apparatus including the magnetic tape cartridge.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a disposition example of a data band and a servo band.

FIG. 2 shows a disposition example of a servo pattern of a linear-tape-open (LTO) Ultrium format tape.

FIG. 3 is a schematic view showing an example of a magnetic tape apparatus.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Magnetic Tape

An aspect of the present invention relates to a magnetic tape having a non-magnetic support and a magnetic layer containing a ferromagnetic powder, in which the magnetic layer has a plurality of servo bands, a region sandwiched between two adjacent servo bands is called a data band, and the minimum value of the TDStens among the five TDStens measured respectively under the five environments described above is 1.43 μm/N or more, a ratio of a change of the TDStens to a change of a relative humidity obtained from the five TDStens is 0.005 μm/N/% or less, and a ratio of a change of the TDStens to a change of the temperature obtained from the five TDStens is 0.020 μm/N/° C. or less. The TDStens is a ratio of a change of a servo band interval to a change of a tension obtained from a plurality of servo band intervals measured by respectively applying a plurality of different tensions in a longitudinal direction of a magnetic tape as a value based on a magnetic tape with a ½ inch width and four total data bands.

In a magnetic tape apparatus which controls a dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape, the larger the tension is applied in the longitudinal direction of the magnetic tape, the larger the dimension in the width direction of the magnetic tape can be shrunk (that is, the width can be made narrower), and the smaller the tension is, the smaller the degree of the shrunk. By adjusting the tension applied in the longitudinal direction of the magnetic tape in this manner, the dimension in the width direction of the magnetic tape can be controlled.

The present inventors have paid attention to the fact that a tape dimensional stability of the magnetic tape in a state in which tension is applied in the longitudinal direction of the magnetic tape can be changed depending on a difference in the measurement environment, in the course of repeated studies to obtain the magnetic tape in which recording and/or reproduction can be performed satisfactorily by adjusting tension applied in the longitudinal direction of the magnetic tape and controlling the dimension in the width direction of the magnetic tape. As a result of further intensive investigation, the dimensional stability of the magnetic tape in a state in which tension is applied in the longitudinal direction of the tape, which is measured under various environments in which the magnetic tape can be placed in use and/or storage, has been determined as an index. This index is the above TDStens. “TDS” is an abbreviation for “tape dimensional stability”, and “tens” is an abbreviation for “tension”. The inventors of the present invention suppose that the easier it is to change the dimension in the width direction of the magnetic tape by applying the tension in the longitudinal direction of the magnetic tape, the easier it is to control the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape. The minimum value of the TDStens among the five TDStens measured under each of the above five environments is 1.43 μm/N or more, which indicates that the dimension in the width direction of the magnetic tape can be easily changed by applying the tension to the longitudinal direction of the magnetic tape under various temperature and humidity environments. The present inventors believe that this contributes to making it easier to control the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape. Further, the inventors of the present invention suppose that a degree of variation of the TDStens due to a difference in temperature and humidity is small, which contributes to making it easier to control the running in a case where the magnetic tape is run for recording and/or reproduction in the magnetic tape apparatus. The indexes relating to this point are the ratio of the change of the TDStens to the change in the relative humidity and the ratio of the change of the TDStens to the change in the temperature.

The above is a supposition of the inventors of the present invention related to the reason why, according to the magnetic tape in which the minimum value of the TDStens among the above five TDStens, the ratio of the change of the TDStens to the change of the relative humidity, and the ratio of the change of the TDStens to the change of the temperature are within the range described above, it is possible to control the dimension in the width direction of the magnetic tape for performing the recording and/or reproduction satisfactorily by adjusting the tension applied to the longitudinal direction of the magnetic tape. However, the present invention is not limited to the above supposition. In addition, the present invention is not limited to the supposition described in the present specification.

Hereinafter, the magnetic tape will be described later in detail.

Method of Measuring TDStens

The TDStens is obtained by the following method in each of the five environments shown above. The above five environments are examples of various environments in which the magnetic tape can be placed during use and/or storage, and the environment in which the magnetic tape is placed during use and/or storage is not limited.

A magnetic tape cartridge accommodating the magnetic tape to be measured is placed in the same environment for at least 5 days in order to adapt the magnetic tape cartridge to the measurement environment. Thereafter, in the magnetic tape apparatus having a tension adjusting mechanism for applying tension in the longitudinal direction of the magnetic tape in the measurement environment, the magnetic tape is made to run in a state of applying tension of 0.2 N in the longitudinal direction of the magnetic tape, an interval between two servo bands adjacent to each other across the data band is obtained for each LPOS word, and the servo band interval is obtained as an arithmetic average of the servo band intervals for all LPOS words obtained for the entire servo band intervals in a case where a plurality of servo band intervals exist over the entire range in the longitudinal direction of a tape having a length of 100 m at a random position of the magnetic tape. The interval between two servo bands adjacent to each other across the data band can be determined, for example, by using a position error signal (PES) obtained from a servo signal obtained by reading a servo pattern with a servo signal reading element. With respect to details, the description of the Examples below can be referred to. The number of servo band intervals is the same as the number of data bands.

In a case where the total number of data bands is 4, the number of servo band intervals is also 4. The servo band interval thus measured is hereinafter referred to as “G_(0.2N)”. A value of the tension applied in the longitudinal direction of the magnetic tape described in the present invention and the present specification is a set value set in the magnetic tape apparatus.

After measuring G_(0.2N), the tension applied in the longitudinal direction of the magnetic tape is increased to 0.4N, and the servo band interval is measured in the same manner as described above in a state in which the tension of 0.4N is applied. The servo band interval thus measured is hereinafter referred to as “G_(0.4N)”.

After measuring G_(0.4N), the tension applied in the longitudinal direction of the magnetic tape is increased to 0.6N, and the servo band interval is measured in the same manner as described above in a state in which the tension of 0.6N is applied. The servo band interval thus measured is hereinafter referred to as “G_(0.6N)”.

After measuring G_(0.6N), the tension applied in the longitudinal direction of the magnetic tape is increased to 0.8N, and the servo band interval is measured in the same manner as described above in a state in which the tension of 0.8N is applied. The servo band interval thus measured is hereinafter referred to as “G_(0.8N)”.

After measuring G_(0.8N), the tension applied in the longitudinal direction of the magnetic tape is increased to 1.0N, and the servo band interval is measured in the same manner as described above in a state in which the tension of 1.0N is applied. The servo band interval thus measured is hereinafter referred to as “G_(1.0N)”.

After measuring G_(1.0N), the tension applied in the longitudinal direction of the magnetic tape is increased to 1.2N, and the servo band interval is measured in the same manner as described above in a state in which the tension of 1.2N is applied. The servo band interval thus measured is hereinafter referred to as “G_(1.2N)”.

The measurement of G_(0.2N), G_(0.4N), G_(0.6N), G_(0.8N), G_(1.0N), and G_(1.2N) is performed within 5 minutes, respectively, and the measurement at each tension is started within 5 minutes after the measurement at the previous tension is ended.

With respect to the G_(0.2N), G_(0.4N), G_(0.6N), G_(0.8N), G_(1.0N), and G_(1.2N) obtained by the above method, the ratio of the change of the servo band interval to the change of tension is obtained. More specifically, a slope A obtained by the least-squares method using the servo band intervals obtained in a state where the tension is applied as X of the linear function Y=AX+B (A is a slope, B is an intercept) and Y is defined as the “TDStens” which is the ratio of the change of the servo band interval to the change of tension in the measurement environment.

The above measurement is performed in the above five environments. Thus, the “TDStens” which is the ratio of the change of the servo band interval to the change of tension in the five environments is obtained. In the present invention and the present specification, the “TDStens” is the value based on the magnetic tape having a width of ½ inch and four total data bands. In a case where the magnetic tape to be measured is the magnetic tape having a width of ½ inch and four total data bands, the ratio of the change of the servo band interval to the change of tension obtained for the magnetic tape is defined as the “TDStens”. On the other hand, in a case where the tape width and/or the total number of data bands are different from the reference, the ratio of the change of the servo band interval to the change of tension obtained by the above method is defined as W (units: mm) for the width of the magnetic tape and D for the total number of data bands, and the value calculated as the “ratio of change of servo band interval to change of tension×[(D/4)/(W/12.65)]” is defined as the “TDStens”. As the width value of the magnetic tape, the width determined for the magnetic tape to be measured can be adopted according to the standard such as linear tape-open (LTO).

For example, for a standard magnetic tape that employs a ½ inch width magnetic tape, ½ inch can be adopted as the width value of the magnetic tape.

In addition, the ratio of the change of TDStens to the change of relative humidity is the TDStens as y of the linear function y=ax+b (a is a slope, b is an intercept) for the value of five TDStens obtained in the above five environments, and x is the slope a obtained by the least-squares method using the relative humidity of the environment for which the TDStens has been obtained.

The ratio of the change of TDStens to the change of temperature is the TDStens as y of the linear function y=cx+d (c is a slope, d is an intercept) for the value of five TDStens obtained in the above five environments, and x is the slope c obtained by the least-squares method using the temperature of the environment for which the TDStens has been obtained.

Minimum value of TDStens

In the above magnetic tape, the minimum value of TDStens among the five TDStens measured under the five environments by the method described above is 1.43 μm/N or more. The present inventors believe that this tendency to easily deform in the width direction to the tension applied in the longitudinal direction contributes to making it easier to control the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape. From this viewpoint, the minimum value of TDStens is preferably 1.45 μm/N or more, more preferably 1.50 μm/N or more, and still more preferably 1.60 μm/N or more. In addition, from the viewpoint of step suitability in manufacturing the magnetic tape, the minimum value of TDStens is preferably 3.00 μm/N or less, more preferably 2.70 μm/or less, still more preferably 2.50 μm/N or less, still more preferably 2.30 μm/N or less, and further more preferably 2.00 μm/N or less.

Ratio of change of TDStens to change of relative humidity

In the above magnetic tape, the ratio of the change of the TDStens to the change of the relative humidity obtained from the above five TDStens is 0.005 μm/N/% or less. The present inventors believe that this also contributes to enabling the recording and/or reproduction satisfactorily by adjusting the tension applied in the longitudinal direction of the magnetic tape and controlling the dimension in the width direction of the magnetic tape. From this viewpoint, the ratio of the change of TDStens to the change of the relative humidity is preferably 0.004 μm/N/% or less, and more preferably 0.003 μm/N/% or less. In addition, the ratio of the change of TDStens to the change of the relative humidity can be, for example, 0 μm/N/%, 0 μm/N/% or more, more than 0 μm/N/%, or 0.001 μm/N/% or more.

Ratio of Change of TDStens to Change of Temperature

In the above magnetic tape, the ratio of the change of the TDStens to the change of the temperature obtained from the above five TDStens is 0.020 μm/N/% or less. The present inventors believe that this also contributes to enabling the recording and/or reproduction satisfactorily by adjusting the tension applied in the longitudinal direction of the magnetic tape and controlling the dimension in the width direction of the magnetic tape. From this viewpoint, the ratio of the change of TDStens to the change of temperature is preferably 0.019 μm/N/% or less, more preferably 0.018 μm/N/% or less, still more preferably 0.017 μm/N/% or less, and further more preferably 0.016 μm/N/% or less. In addition, the ratio of the change of TDStens to the change of the temperature can be, for example, 0 μm/N/%, 0 μm/N/% or more, more than 0 μm/N/%, or 0.001 μm/N/% or more, and 0.010 μm or more.

These various values can be adjusted, for example, by the tape thickness (total thickness) of the magnetic tape, the intensity (for example, Young's modulus) of the non-magnetic support, the moisture content of the non-magnetic support, the manufacturing conditions of the magnetic tape, and the like. Regarding this point, the description below can be referred to.

Non-Magnetic Support

As the non-magnetic support (hereinafter, also simply referred to as a “support”), well-known components such as polyethylene terephthalate, polyethylene naphthalate, polyamide, polyamide imide, and aromatic polyamide subjected to biaxial stretching are used. Among these, polyethylene terephthalate, and polyethylene naphthalate are preferable.

The non-magnetic support of the magnetic tape may, in one aspect, be an aromatic polyester support. In the present invention and the present specification, an “aromatic polyester” means a resin including an aromatic skeleton and a plurality of ester bonds, and the “aromatic polyester support” means a support including at least one layer of an aromatic polyester film. The “aromatic polyester film” is defined as a film in which the component that occupies the most on a mass basis among the components constituting this film is the aromatic polyester. The “aromatic polyester support” in the present invention and the present specification includes those in which the resin films contained in the support are all aromatic polyester films, and those in which the resin films include aromatic polyester films and other resin films. Specific aspects of the aromatic polyester support include a single layer aromatic polyester film, a laminated film of aromatic polyester films with two or more layers having the same constituent component, a laminated film of aromatic polyester films with two or more layers having different constituent components, a laminated film including aromatic polyester films with one or more layers and resin films other than aromatic polyesters with one or more layers, and the like. An adhesive layer or the like may be randomly included between two adjacent layers in the laminated film. In addition, the aromatic polyester support may randomly include a metal film and/or a metal oxide film formed on one or both surfaces by vapor deposition or the like. The same applies to the “polyethylene terephthalate support” and the “polyethylene naphthalate support” in the present invention and the present specification.

An aromatic ring contained in the aromatic skeleton of the aromatic polyester is not particularly limited. Specific examples of the aromatic ring include a benzene ring and a naphthalene ring.

For example, polyethylene terephthalate (PET) is a polyester containing a benzene ring and is a resin obtained by polycondensation of ethylene glycol and terephthalic acid and/or dimethyl terephthalate. The “polyethylene terephthalate” in the present invention and the present specification includes structures having one or more other components (for example, copolymerizing components, components introduced at a terminal or a side chain, and the like) in addition to the above components.

The polyethylene naphthalate (PEN) is a polyester containing the naphthalene ring, and is a resin obtained by carrying out an esterification reaction of dimethyl 2,6-naphthalenedicarboxylate with ethylene glycol, and then carrying out a transesterification reaction and a polycondensation reaction. The “polyethylene naphthalate” in the present invention and the present specification includes structures having one or more other components (for example, copolymerizing components, components introduced at a terminal or a side chain, and the like) in addition to the above components.

In addition, the non-magnetic support can be a biaxial stretching film, and may be a film that has been subjected to corona discharge, plasma treatment, easy adhesion treatment, heat treatment, or the like.

An index of physical properties of the non-magnetic support includes, for example, a moisture content. In the present invention and the present specification, the moisture content of the non-magnetic support is a value obtained by the following method. The moisture content shown in the table below is a value obtained by the following method.

A sample piece (for example, a sample piece with a mass of several grams) cut out from the non-magnetic support to be measured for the moisture content is dried to constant mass in a vacuum dryer having a temperature of 180° C. and a pressure of 100 Pa (Pascal) or less. The mass of the sample piece dried in this way is denoted by W1. W1 is a value measured in a measurement environment of a temperature of 23° C. and a relative humidity of 50% within 30 seconds after being taken out from the vacuum dryer. Next, the mass after placing this sample piece in an environment of a temperature of 25° C. and a relative humidity of 75% for 48 hours is denoted by W2. W2 is a value measured in a measurement environment of a temperature of 23° C. and a relative humidity of 50% within 30 seconds after being taken out from the environment. The moisture content is calculated by the following formula. Moisture content (%)=[(W2−W1)/W1]×100

For example, the moisture content of the non-magnetic support can be obtained by the above-described method after removing a part of the magnetic tape other than the non-magnetic support such as a magnetic layer by a known method (for example, film removal using organic solvent).

In one aspect, the moisture content of the non-magnetic support of the magnetic tape is preferably 1.00% or less, more preferably 0.80% or less, and still more preferably 0.60 or less. In addition, the moisture content of the non-magnetic support of the magnetic tape may be 0%, 0% or more, more than 0%, or 0.10% or more. By using a non-magnetic support having a low moisture content, the ratio of a change of TDStens to a change of a relative humidity and/or temperature tends to be small.

An index of physical properties of the non-magnetic support includes, for example, an Young's modulus. In the present invention and the present specification, the Young's modulus of the non-magnetic support is a value measured by the following method in a measurement environment of a temperature of 23° C. and a relative humidity of 50%. The Young's modulus shown in the table below is a value obtained by the following method using Tensilon manufactured by Toyo Baldwin as a universal tensile testing apparatus.

The sample piece cut out from the non-magnetic support to be measured is pulled by the universal tensile testing apparatus under the conditions of a chuck-to-chuck distance of 100 mm, a tensile speed of 10 mm/min, and a chart speed of 500 mm/min. As the universal tensile testing apparatus, for example, a commercially available universal tensile testing apparatus such as Tensilon manufactured by Toyo Baldwin, or a universal tensile testing apparatus having a known configuration can be used. From a tangent line of a rising portion of a load-elongation curve obtained in this way, the Young's modulus in the longitudinal direction and the width direction of the sample piece is calculated. Here, the longitudinal direction and the width direction of the sample piece mean the longitudinal direction and the width direction in a case where the sample piece is included in the magnetic tape.

For example, the Young's modulus in the longitudinal direction and the width direction of the non-magnetic support can be obtained by the above-described method after removing a part of the magnetic tape other than the non-magnetic support such as a magnetic layer by a known method (for example, film removal using organic solvent).

In one aspect, the Young's modulus of the non-magnetic support of the magnetic tape in the longitudinal direction is preferably 3000 MPa or more, more preferably 5000 MPa or more, and still more preferably 7000 MPa or more. In addition, the Young's modulus of the non-magnetic support of the magnetic tape in the longitudinal direction may be 15000 MPa or less, 13000 MPa or less, or 11000 MPa or less. In the width direction, the Young's modulus of the non-magnetic support of the magnetic tape in the width direction is preferably 2000 MPa or more, more preferably 3000 MPa or more, and still more preferably 4000 MPa or more. In addition, the Young's modulus of the non-magnetic support of the magnetic tape in the width direction may be 10000 MPa or less, 8000 MPa or less, or 6000 MPa or less. In a case where manufacturing the magnetic tape, the non-magnetic support is usually used with a machine direction (MD) of the film as the longitudinal direction and a transverse direction (TN) as the width direction. Further, in one aspect, from the viewpoint of increasing the TDStens, the Young's modulus in the longitudinal direction is preferably larger than the Young's modulus in the width direction, and a difference (the Young's modulus in the longitudinal direction—the Young's modulus in the width direction) is more preferably in the range of 1500 MPa to 5000 MPa.

The moisture content and Young's modulus of the non-magnetic support can be controlled by the type and mixing ratio of the components constituting the support, the manufacturing conditions of the support, and the like. For example, the Young's modulus in the longitudinal direction and the Young's modulus in the width direction can be controlled respectively by adjusting a stretching ratio in each direction in a biaxial stretching treatment.

Magnetic Layer

Ferromagnetic Powder

As the ferromagnetic powder contained in the magnetic layer, one or a combination of two or more kinds of ferromagnetic powder known as the ferromagnetic powder used in the magnetic layer of various magnetic recording medium can be used. It is preferable to use ferromagnetic powder having a small average particle size, from a viewpoint of improvement of recording density. In this respect, an average particle size of the ferromagnetic powder is preferably 50 nm or less, more preferably 45 nm or less, still more preferably 40 nm or less, still more preferably 35 nm or less, still more preferably 30 nm or less, still more preferably 25 nm or less, and still more preferably 20 nm or less. On the other hand, from a viewpoint of magnetization stability, an average particle size of the ferromagnetic powder is preferably 5 nm or more, more preferably 8 nm or more, still more preferably 10 nm or more, and still more preferably 15 nm or more, and still more preferably 20 nm or more.

Hexagonal Ferrite Powder

Preferable specific examples of the ferromagnetic powder may include a hexagonal ferrite powder.

For details of the hexagonal ferrite powder, descriptions disclosed in paragraphs [0012] to [0030] of JP2011-225417A, paragraphs [0134] to [0136] of JP2011-216149A, paragraphs [0013] to [0030] of JP2012-204726A, and paragraphs [0029] to [0084] of JP2015-127985A can be referred to, for example.

In the present invention and the present specification, the “hexagonal ferrite powder” refers to the ferromagnetic powder in which a hexagonal ferrite type crystal structure is detected as a main phase by an X-ray diffraction analysis. The main phase refers to a structure to which the highest intensity diffraction peak in an X-ray diffraction spectrum obtained by the X-ray diffraction analysis is attributed. For example, in a case where the highest intensity diffraction peak is attributed to the hexagonal ferrite type crystal structure in an X-ray diffraction spectrum obtained by X-ray diffraction analysis, it is determined that the hexagonal ferrite type crystal structure is detected as the main phase. In a case where only a single structure is detected by the X-ray diffraction analysis, this detected structure is taken as the main phase. The hexagonal ferrite type crystal structure includes at least an iron atom, a divalent metal atom, and an oxygen atom, as a constituent atom. The divalent metal atom is a metal atom that can be a divalent cation as an ion, and examples thereof may include an alkaline earth metal atom such as a strontium atom, a barium atom, and a calcium atom, a lead atom, and the like. In the present invention and the present specification, the hexagonal strontium ferrite powder means that a main divalent metal atom contained in the powder is a strontium atom, and hexagonal barium ferrite powder means that a main divalent metal atom included in the powder is a barium atom. The main divalent metal atom refers to a divalent metal atom that occupies the most on an at % basis among divalent metal atoms included in the powder. Here, a rare earth atom is not included in the above divalent metal atom. The “rare earth atom” in the present invention and the present specification is selected from the group consisting of a scandium atom (Sc), a yttrium atom (Y), and a lanthanoid atom. The Lanthanoid atom is selected from the group consisting of a lanthanum atom (La), a cerium atom (Ce), a praseodymium atom (Pr), a neodymium atom (Nd), a promethium atom (Pm), a samarium atom (Sm), an europium atom (Eu), a gadolinium atom (Gd), a terbium atom (Tb), a dysprosium atom (Dy), a holmium atom (Ho), an erbium atom (Er), a thulium atom (Tm), an ytterbium atom (Yb), and a lutetium atom (Lu).

Hereinafter, the hexagonal strontium ferrite powder which is one aspect of the hexagonal ferrite powder will be described in more detail.

An activation volume of the hexagonal strontium ferrite powder is preferably in a range of 800 to 1600 nm³. The fine particulate hexagonal strontium ferrite powder exhibiting an activation volume in the above range is suitable for manufacturing a magnetic tape exhibiting excellent electromagnetic conversion characteristics.

An activation volume of the hexagonal strontium ferrite powder is preferably 800 nm³ or more, and may be, for example, 850 nm³ or more. Further, from a viewpoint of further improving electromagnetic conversion characteristics, an activation volume of the hexagonal strontium ferrite powder is more preferably 1500 nm³ or less, still more preferably 1400 nm³ or less, still more preferably 1300 nm³ or less, still more preferably 1200 nm³ or less, and still more preferably 1100 nm³ or less. The same applies to an activation volume of the hexagonal barium ferrite powder.

The “activation volume” is a unit of magnetization reversal and is an index indicating a magnetic size of a particle. An activation volume described in the present invention and the specification and an anisotropy constant Ku which will be described later are values obtained from the following relational expression between a coercivity Hc and an activation volume V, by performing measurement in an Hc measurement portion at a magnetic field sweep rate of 3 minutes and 30 minutes using a vibrating sample magnetometer (measurement temperature: 23° C.±1°C.). In a unit of the anisotropy constant Ku, 1 erg/cc=1.0×10⁻¹ J/m³. Hc=2Ku/Ms{1−[(kT/KuV)ln(At/0.693)]^(1/2)}

[In the formula, Ku: anisotropy constant (unit: J/m³), Ms: saturation magnetization (Unit: kA/m), k: Boltzmann constant, T: absolute temperature (unit: K), V: activation volume (unit: cm³), A: spin precession frequency (unit: s⁻¹), t: magnetic field reversal time (unit: s)]

An index for reducing thermal fluctuation, in other words, improving thermal stability can include the anisotropy constant Ku. The hexagonal strontium ferrite powder may preferably have Ku of 1.8×10⁵ J/m³ or more, and more preferably have a Ku of 2.0×10⁵ J/m³ or more. In addition, Ku of the hexagonal strontium ferrite powder may be, for example, 2.5×10⁵ J/m³ or less. Here, it means that the higher Ku is, the higher thermal stability is, this is preferable, and thus, a value thereof is not limited to the values exemplified above.

The hexagonal strontium ferrite powder may or may not include a rare earth atom. In a case where the hexagonal strontium ferrite powder includes a rare earth atom, it is preferable to include a rare earth atom at a content (bulk content) of 0.5 to 5.0 at % with respect to 100 at % of an iron atom. In one aspect, the hexagonal strontium ferrite powder containing rare earth atoms may have an uneven distribution property of a rare earth atom surface layer portion. In the present invention and the present specification, the “rare earth atom surface layer portion uneven distribution property” means that a rare earth atom content with respect to 100 at % of an iron atom in a solution obtained by partially dissolving the hexagonal strontium ferrite powder with an acid (hereinafter, referred to as a “rare earth atom surface layer portion content” or simply a “surface layer portion content” for a rare earth atom) and a rare earth atom content with respect to 100 at % of an iron atom in a solution obtained by totally dissolving the hexagonal strontium ferrite powder with an acid (hereinafter, referred to as a “rare earth atom bulk content” or simply a “bulk content” for a rare earth atom) satisfy a ratio of a rare earth atom surface layer portion content/a rare earth atom bulk content >1.0. A rare earth atom content in the hexagonal strontium ferrite powder which will be described later is the same meaning as the rare earth atom bulk content. On the other hand, partial dissolution using an acid dissolves a surface layer portion of a particle configuring the hexagonal strontium ferrite powder, and thus, a rare earth atom content in a solution obtained by partial dissolution is a rare earth atom content in a surface layer portion of a particle configuring the hexagonal strontium ferrite powder. A rare earth atom surface layer portion content satisfying a ratio of “rare earth atom surface layer portion content/rare earth atom bulk content >1.0” means that in a particle of the hexagonal strontium ferrite powder, rare earth atoms are unevenly distributed in a surface layer portion (that is, more than an inside). The surface layer portion in the present invention and the present specification means a partial region from a surface of a particle configuring the hexagonal strontium ferrite powder toward an inside.

In a case where the hexagonal strontium ferrite powder includes a rare earth atom, a rare earth atom content (bulk content) is preferably in a range of 0.5 to 5.0 at % with respect to 100 at % of an iron atom. It is considered that a bulk content in the above range of the included rare earth atom and uneven distribution of the rare earth atoms in a surface layer portion of a particle configuring the hexagonal strontium ferrite powder contribute to suppression of a decrease in a reproducing output in repeated reproduction. It is supposed that this is because the hexagonal strontium ferrite powder includes a rare earth atom with a bulk content in the above range, and rare earth atoms are unevenly distributed in a surface layer portion of a particle configuring the hexagonal strontium ferrite powder, and thus it is possible to increase an anisotropy constant Ku. The higher a value of an anisotropy constant Ku is, the more a phenomenon called so-called thermal fluctuation can be suppressed (in other words, thermal stability can be improved). By suppressing occurrence of thermal fluctuation, it is possible to suppress a decrease in reproducing output during repeated reproduction. It is supposed that uneven distribution of rare earth atoms in a particulate surface layer portion of the hexagonal strontium ferrite powder contributes to the stabilization of spins of iron (Fe) sites in a crystal lattice of a surface layer portion, and thus, an anisotropy constant Ku may be increased.

Moreover, it is supposed that the use of hexagonal strontium ferrite powder having a rare earth atom surface layer portion uneven distribution property as a ferromagnetic powder in the magnetic layer also contributes to inhibition of a surface of the magnetic layer from being scraped by being slid with respect to the magnetic head. That is, it is supposed that the hexagonal strontium ferrite powder having rare earth atom surface layer portion uneven distribution property can also contribute to an improvement of running durability of the magnetic tape. It is supposed that this may be because uneven distribution of rare earth atoms on a surface of a particle configuring the hexagonal strontium ferrite powder contributes to an improvement of interaction between the particle surface and an organic substance (for example, a binding agent and/or an additive) included in the magnetic layer, and, as a result, an intensity of the magnetic layer is improved.

From a viewpoint of further suppressing a decrease in reproducing output during repeated reproduction and/or a viewpoint of further improving the running durability, the rare earth atom content (bulk content) is more preferably in a range of 0.5 to 4.5 at %, still more preferably in a range of 1.0 to 4.5 at %, and still more preferably in a range of 1.5 to 4.5 at %.

The bulk content is a content obtained by totally dissolving hexagonal strontium ferrite powder. In the present invention and the present specification, unless otherwise noted, the content of an atom means a bulk content obtained by totally dissolving the hexagonal strontium ferrite powder. The hexagonal strontium ferrite powder including a rare earth atom may include only one kind of rare earth atom as the rare earth atom, or may include two or more kinds of rare earth atoms. The bulk content in the case of including two or more kinds of rare earth atoms is obtained for the total of two or more kinds of rare earth atoms. This also applies to other components in the present invention and the present specification. That is, unless otherwise noted, a certain component may be used alone or in combination of two or more. A content amount or content in the case where two or more components are used refers to that for the total of two or more components.

In a case where the hexagonal strontium ferrite powder includes a rare earth atom, the included rare earth atom may be any one or more of rare earth atoms. As a rare earth atom that is preferable from a viewpoint of further suppressing a decrease in reproducing output in repeated reproduction, there are a neodymium atom, a samarium atom, a yttrium atom, and a dysprosium atom, here, a neodymium atom, a samarium atom, and a yttrium atom are more preferable, and a neodymium atom is still more preferable.

In the hexagonal strontium ferrite powder having a rare earth atom surface layer portion uneven distribution property, the rare earth atoms may be unevenly distributed in the surface layer portion of a particle configuring the hexagonal strontium ferrite powder, and the degree of uneven distribution is not limited. For example, for a hexagonal strontium ferrite powder having a rare earth atom surface layer portion uneven distribution property, a ratio between a surface layer portion content of a rare earth atom obtained by partial dissolution under dissolution conditions which will be described later and a bulk content of a rare earth atom obtained by total dissolution under dissolution conditions which will be described later, that is, “surface layer portion content/bulk content” exceeds 1.0 and may be 1.5 or more. A “surface layer portion content/bulk content” larger than 1.0 means that in a particle configuring the hexagonal strontium ferrite powder, rare earth atoms are unevenly distributed in the surface layer portion (that is, more than the inside). Further, a ratio between a surface layer portion content of a rare earth atom obtained by partial dissolution under dissolution conditions which will be described later and a bulk content of a rare earth atom obtained by total dissolution under the dissolution conditions which will be described later, that is, “surface layer portion content/bulk content” may be, for example, 10.0 or less, 9.0 or less, 8.0 or less, 7.0 or less, 6.0 or less, 5.0 or less, or 4.0 or less. Here, in the hexagonal strontium ferrite powder having a rare earth atom surface layer portion uneven distribution property, the rare earth atoms may be unevenly distributed in the surface layer portion of a particle configuring the hexagonal strontium ferrite powder, and the “surface layer portion content/bulk content” is not limited to the illustrated upper limit or lower limit.

The partial dissolution and the total dissolution of the hexagonal strontium ferrite powder will be described below. For the hexagonal strontium ferrite powder that exists as a powder, the partially and totally dissolved sample powder is taken from the same lot of powder. On the other hand, for the hexagonal strontium ferrite powder included in the magnetic layer of the magnetic tape, a part of the hexagonal strontium ferrite powder taken out from the magnetic layer is subjected to partial dissolution, and the other part is subjected to total dissolution. The hexagonal strontium ferrite powder can be taken out from the magnetic layer by a method disclosed in a paragraph [0032] of JP2015-091747A, for example.

The partial dissolution means that dissolution is performed such that, at the end of dissolution, the residue of the hexagonal strontium ferrite powder can be visually checked in the solution. For example, by partial dissolution, it is possible to dissolve a region of 10 to 20 mass % of the particle configuring the hexagonal strontium ferrite powder with the total particle being 100 mass %. On the other hand, the total dissolution means that dissolution is performed such that, at the end of dissolution, the residue of the hexagonal strontium ferrite powder cannot be visually checked in the solution.

The partial dissolution and measurement of the surface layer portion content are performed by the following method, for example. Here, the following dissolution conditions such as an amount of sample powder are illustrative, and dissolution conditions for partial dissolution and total dissolution can be employed in any manner.

A container (for example, a beaker) containing 12 mg of sample powder and 10 ml of 1 mol/L hydrochloric acid is held on a hot plate at a set temperature of 70° C. for 1 hour. The obtained solution is filtered by a membrane filter of 0.1 μm. Elemental analysis of the obtained filtrate is performed by an inductively coupled plasma (ICP) analyzer. In this way, the surface layer portion content of a rare earth atom with respect to 100 at % of an iron atom can be obtained. In a case where a plurality of kinds of rare earth atoms are detected by elemental analysis, the total content of all rare earth atoms is defined as the surface layer portion content. This also applies to the measurement of the bulk content.

On the other hand, the total dissolution and measurement of the bulk content are performed by the following method, for example.

A container (for example, a beaker) containing 12 mg of sample powder and 10 ml of 4 mol/L hydrochloric acid is held on a hot plate at a set temperature of 80° C. for 3 hours. Thereafter, the method is carried out in the same manner as the partial dissolution and the measurement of the surface layer portion content, and the bulk content with respect to 100 at % of an iron atom can be obtained.

From a viewpoint of increasing the reproducing output in a case of reproducing data recorded on the magnetic tape, it is desirable that mass magnetization σs of the ferromagnetic powder included in the magnetic tape is high. In this regard, the hexagonal strontium ferrite powder including a rare earth atom but not having the rare earth atom surface layer portion uneven distribution property tends to have as largely lower than the hexagonal strontium ferrite powder including no rare earth atom. On the other hand, it is considered that hexagonal strontium ferrite powder having a rare earth atom surface layer portion uneven distribution property is preferable in suppressing such a large decrease in σs. In one aspect, σs of the hexagonal strontium ferrite powder may be 45 A·m²/kg or more, and may be 47 A·m²/kg or more. On the other hand, from a viewpoint of noise reduction, σs is preferably 80 A·m²/kg or less and more preferably 60 A·m²/kg or less, σs can be measured using a known measuring apparatus, such as a vibrating sample magnetometer, capable of measuring magnetic characteristics. In the present invention and the present specification, unless otherwise noted, the mass magnetization σs is a value measured at a magnetic field intensity of 15 kOe. 1 [kOe]=10⁶/4π [A/m].

Regarding the content (bulk content) of a constituent atom of the hexagonal strontium ferrite powder, the strontium atom content may be, for example, in a range of 2.0 to 15.0 at % with respect to 100 at % of an iron atom. In one aspect, in the hexagonal strontium ferrite powder, a divalent metal atom included in the powder may be only a strontium atom. In another aspect, the hexagonal strontium ferrite powder may include one or more other divalent metal atoms in addition to a strontium atom. For example, a barium atom and/or a calcium atom may be included. In a case where another divalent metal atom other than a strontium atom is included, a barium atom content and a calcium atom content in the hexagonal strontium ferrite powder are, for example, in a range of 0.05 to 5.0 at % with respect to 100 at % of an iron atom, respectively.

As a crystal structure of hexagonal ferrite, a magnetoplumbite type (also referred to as an “M-type”), a W type, a Y type, and a Z type are known. The hexagonal strontium ferrite powder may have any crystal structure. The crystal structure can be checked by X-ray diffraction analysis. In the hexagonal strontium ferrite powder, a single crystal structure or two or more crystal structures may be detected by X-ray diffraction analysis. For example, according to one aspect, in the hexagonal strontium ferrite powder, only the M-type crystal structure may be detected by X-ray diffraction analysis. For example, M-type hexagonal ferrite is represented by a composition formula of AFe₁₂O₁₉. Here, A represents a divalent metal atom, and in a case where the hexagonal strontium ferrite powder is the M-type, A is only a strontium atom (Sr), or in a case where, as A, a plurality of divalent metal atoms are included, as described above, a strontium atom (Sr) occupies for the most on an at % basis. The divalent metal atom content of the hexagonal strontium ferrite powder is usually determined by the type of crystal structure of the hexagonal ferrite and is not particularly limited. The same applies to the iron atom content and the oxygen atom content. The hexagonal strontium ferrite powder may include at least an iron atom, a strontium atom, and an oxygen atom, and may further include a rare earth atom. Furthermore, the hexagonal strontium ferrite powder may or may not include atoms other than these atoms. As an example, the hexagonal strontium ferrite powder may include an aluminum atom (Al). A content of an aluminum atom can be, for example, 0.5 to 10.0 at % with respect to 100 at % of an iron atom. From a viewpoint of further suppressing a decrease in reproducing output in repeated reproduction, the hexagonal strontium ferrite powder includes an iron atom, a strontium atom, an oxygen atom, and a rare earth atom, and the content of atoms other than these atoms is preferably 10.0 at % or less, more preferably in a range of 0 to 5.0 at %, and may be 0 at % with respect to 100 at % of an iron atom. That is, in one aspect, the hexagonal strontium ferrite powder may not include atoms other than an iron atom, a strontium atom, an oxygen atom, and a rare earth atom. The content expressed in at % is obtained by converting a content of each atom (unit: mass %) obtained by totally dissolving hexagonal strontium ferrite powder into a value expressed in at % using an atomic weight of each atom. Further, in the present invention and present specification, “not include” for a certain atom means that a content measured by an ICP analyzer after total dissolution is 0 mass %. A detection limit of the ICP analyzer is usually 0.01 ppm (parts per million) or less on a mass basis. The “not included” is used as a meaning including that an atom is included in an amount less than the detection limit of the ICP analyzer. In one aspect, the hexagonal strontium ferrite powder may not include a bismuth atom (Bi).

Metal Powder

As a preferred specific example of the ferromagnetic powder, a ferromagnetic metal powder can also be used. For details of the ferromagnetic metal powder, descriptions disclosed in paragraphs [0137] to [0141] of JP2011-216149A and paragraphs [0009] to [0023] of JP2005-251351A can be referred to, for example.

ε-Iron Oxide Powder

As a preferred specific example of the ferromagnetic powder, ε-iron oxide powder can also be used. In the present invention and the present specification. “ε-iron oxide powder” refers to ferromagnetic powder in which an F-iron oxide type crystal structure is detected as a main phase by X-ray diffraction analysis. For example, in a case where the highest intensity diffraction peak is attributed to an ε-iron oxide type crystal structure in an X-ray diffraction spectrum obtained by X-ray diffraction analysis, it is determined that the ε-iron oxide type crystal structure is detected as the main phase. As a manufacturing method of ε-iron oxide powder, a producing method from a goethite, a reverse micelle method, and the like are known. All of the manufacturing methods are well known. Regarding a method of manufacturing ε-iron oxide powder in which a part of Fe is substituted with substitutional atoms such as Ga, Co, Ti, Al, or Rh, a description disclosed in J. Jpn. Soc. Powder Metallurgy Vol. 61 Supplement, No. S1, pp. S280 to S284, J. Mater. Chem. C, 2013, 1, pp. 5200 to 5206 can be referred to, for example. Here, the manufacturing method of ε-iron oxide powder capable of being used as the ferromagnetic powder in the magnetic layer of the magnetic tape is not limited to the methods described here.

An activation volume of the ε-iron oxide powder is preferably in a range of 300 to 1500 nm³. The fine particulate ε-iron oxide powder exhibiting an activation volume in the above range is suitable for manufacturing a magnetic tape exhibiting excellent electromagnetic conversion characteristics. An activation volume of the ε-iron oxide powder is preferably 300 nm³ or more, and may be, for example, 500 nm³ or more. Further, from a viewpoint of further improving electromagnetic conversion characteristics, an activation volume of the ε-iron oxide powder is more preferably 1400 nm³ or less, still more preferably 1300 nm³ or less, still more preferably 1200 nm³ or less, and still more preferably 1100 nm³ or less.

An index for reducing thermal fluctuation, in other words, improving thermal stability can include the anisotropy constant Ku. The ε-iron oxide powder preferably has Ku of 3.0×10⁴ J/m³ or more, and more preferably has Ku of 8.0×10⁴ J/m³ or more. Ku of the ε-iron oxide powder may be, for example, 3.0×10⁵ J/m³ or less. Here, it means that the higher Ku is, the higher thermal stability is, this is preferable, and thus, a value thereof is not limited to the values exemplified above.

From a viewpoint of increasing the reproducing output in a case of reproducing data recorded on the magnetic tape, it is desirable that mass magnetization σs of the ferromagnetic powder included in the magnetic tape is high. In this regard, in one aspect, σs of the ε-iron oxide powder may be 8 A·m²/kg or more, and may be 12 A·m²/kg or more. On the other hand, from a viewpoint of noise reduction, σs of the ε-iron oxide powder is preferably 40 A·m²/kg or less and more preferably 35 A·m²/kg or less.

In the present invention and the present specification, unless otherwise noted, an average particle size of various powders such as the ferromagnetic powder is a value measured by the following method using a transmission electron microscope.

The powder is imaged at a magnification ratio of 100,000 with a transmission electron microscope, and the image is printed on printing paper so that the total magnification ratio becomes 500,000 to obtain an image of particles configuring the powder. A target particle is selected from the obtained image of particles, an outline of the particle is traced with a digitizer, and a size of the particle (primary particle) is measured. The primary particle is an independent particle which is not aggregated.

The measurement described above is performed regarding 500 particles randomly extracted. An arithmetic average of the particle sizes of 500 particles obtained as described above is an average particle size of the powder. As the transmission electron microscope, a transmission electron microscope H-9000 manufactured by Hitachi, Ltd. can be used, for example. In addition, the measurement of the particle size can be performed by well-known image analysis software, for example, image analysis software KS-400 manufactured by Carl Zeiss. The average particle size shown in Examples which will be described later is a value measured by using a transmission electron microscope H-9000 manufactured by Hitachi, Ltd. as the transmission electron microscope, and image analysis software KS-400 manufactured by Carl Zeiss as the image analysis software, unless otherwise noted. In the present invention and the present specification, the powder means an aggregate of a plurality of particles. For example, ferromagnetic powder means an aggregate of a plurality of ferromagnetic particles. Further, the aggregate of the plurality of particles not only includes an aspect in which particles configuring the aggregate directly come into contact with each other, but also includes an aspect in which a binding agent or an additive which will be described later is sandwiched between the particles. The term “particle” is used for representing a powder in some cases.

As a method of taking sample powder from the magnetic tape in order to measure the particle size, a method disclosed in a paragraph [0015] of JP2011-048878A can be used, for example.

In the present invention and the present specification, unless otherwise noted.

(1) in a case where the shape of the particle observed in the particle image described above is a needle shape, a fusiform shape, or a columnar shape (here, a height is greater than a maximum long diameter of a bottom surface), the size (particle size) of the particles configuring the powder is shown as a length of a long axis configuring the particle, that is, a long axis length, (2) in a case where the shape of the particle is a plate shape or a columnar shape (here, a thickness or a height is smaller than a maximum long diameter of a plate surface or a bottom surface), the particle size is shown as a maximum long diameter of the plate surface or the bottom surface, and

(3) in a case where the shape of the particle is a sphere shape, a polyhedron shape, or an unspecified shape, and the long axis configuring the particles cannot be specified from the shape, the particle size is shown as an equivalent circle diameter. The equivalent circle diameter is a value obtained by a circle projection method.

In addition, regarding an average acicular ratio of the powder, a length of a short axis, that is, a short axis length of each of the particles is measured in the measurement described above, a value (long axis length/short axis length) of each particle is obtained, and an arithmetic average of the values obtained regarding 500 particles is calculated. Here, unless otherwise noted, in a case of (1), the short axis length as the definition of the particle size is a length of a short axis configuring the particle, in a case of (2), the short axis length is a thickness or a height, and in a case of (3), the long axis and the short axis are not distinguished, thus, the value of (long axis length/short axis length) is assumed as 1, for convenience.

In addition, unless otherwise noted, in a case where the shape of the particle is specified, for example, in a case of the definition of the particle size (1), the average particle size is an average long axis length, and in a case of the definition (2), the average particle size is an average plate diameter. In a case of the definition (3), the average particle size is an average diameter (also referred to as an average particle diameter).

A content amount (filling percentage) of the ferromagnetic powder of the magnetic layer is preferably 50 to 90 mass % and more preferably 60 to 90 mass %. A high filling percentage of the ferromagnetic powder in the magnetic layer is preferable from a viewpoint of improvement of recording density.

Binding Agent

The magnetic tape can be a coating type magnetic tape, and include the binding agent in the magnetic layer. The binding agent is one or more kinds of resins. As the binding agent, various resins usually used as a binding agent of a coating type magnetic recording medium can be used. For example, as the binding agent, a resin selected from a polyurethane resin, a polyester resin, a polyamide resin, a vinyl chloride resin, an acrylic resin obtained by copolymerizing styrene, acrylonitrile, methyl methacryate, or the like, a cellulose resin such as nitrocellulose, an epoxy resin, a phenoxy resin, and a polyvinylalkylal resin such as polyvinyl acetal or polyvinyl butyral can be used alone or a plurality of the resins can be mixed with each other to be used. Among these, a polyurethane resin, an acrylic resin, a cellulose resin, and a vinyl chloride resin are preferable. These resins may be homopolymers or copolymers. These resins can be used as the binding agent even in the non-magnetic layer and/or a back coating layer which will be described later.

For the binding agent described above, descriptions disclosed in paragraphs [0028] to [0031] of JP2010-024113A can be referred to. An average molecular weight of the resin used as the binding agent can be, for example, 10,000 or more and 200,000 or less as a weight-average molecular weight. The weight-average molecular weight of the present invention and the present specification is, by gel permeation chromatography (GPC), a value obtained by performing polystyrene conversion of a value measured under the following measurement conditions. The weight-average molecular weight of the binding agent shown in Examples which will be described later is a value obtained by performing polystyrene conversion of a value measured under the following measurement conditions. The binding agent can be used in an amount of, for example, 1.0 to 30.0 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder.

GPC apparatus: HLC-8120 (manufactured by Tosoh Corporation)

Column: TSKgel Multipore HXL-M (manufactured by Tosoh Corporation, 7.8 mm inner diameter (ID)×30.0 cm)

Eluent: Tetrahydrofuran (THF)

Curing Agent

A curing agent can also be used together with a resin usable as the binding agent. As the curing agent, in one aspect, a thermosetting compound which is a compound in which a curing reaction (crosslinking reaction) proceeds due to heating can be used, and in another aspect, a photocurable compound in which a curing reaction (crosslinking reaction) proceeds due to light irradiation can be used. At least a part of the curing agent can be included in the magnetic layer in a state of being reacted (crosslinked) with other components such as the binding agent, by proceeding the curing reaction in a magnetic layer forming step.

The same applies to the layer formed using this composition in a case where the composition used for forming the other layer includes the curing agent. The preferred curing agent is a thermosetting compound, and polyisocyanate is suitable for this. For details of the polyisocyanate, descriptions disclosed in paragraphs [0124] and [0125] of JP2011-216149A can be referred to. The curing agent can be used in a composition for forming the magnetic layer in an amount of, for example, 0 to 80.0 parts by mass, and preferably 50.0 to 80.0 parts by mass, from a viewpoint of improvement of an intensity of the magnetic layer, with respect to 100.0 parts by mass of the binding agent.

Additive

The magnetic layer may include, as necessary, one or more additives. As an example of the additive, the curing agent described above can be used. In addition, examples of the additive which can be included in the magnetic layer include non-magnetic powder (for example, inorganic powder or carbon black), a lubricant, a dispersing agent, a dispersing assistant, a fungicide, an antistatic agent, and an antioxidant. For example, regarding the lubricant, the reference can be made to paragraphs [0030] to [0033], [0035], and [0036] of JP2016-126817A. The lubricant may be contained in the non-magnetic layer described later. For the lubricant that can be contained in the non-magnetic layer, the reference can be made to paragraphs [0030], [0031], and [0034] to [0036] of JP2016-126817A. For the dispersing agent, the reference can be made to paragraphs [0061] and [0071] of JP2012-133837A. The dispersing agent may be added to a composition for forming the non-magnetic layer. For the dispersing agent which can be added in the composition for forming the non-magnetic layer, the reference can be made to a paragraph [006] of JP2012-133837A. In addition, as the non-magnetic powder which can be contained in the magnetic layer, non-magnetic powder which can function as an abrasive, or non-magnetic powder which can function as a protrusion forming agent which forms protrusions suitably protruded from the surface of the magnetic layer (for example, non-magnetic colloidal particles) is used. An average particle size of a colloidal silica (silica colloidal particles) shown in Examples which will be described later is a value obtained by a method disclosed in a paragraph [0015] of JP2011-048878A as a measurement method of an average particle diameter. As the additives, a commercially available product can be suitably selected or manufactured by a well-known method according to the desired properties, and any amount thereof can be used. An example of the additive that can be used to improve the dispersibility of an abrasive in the magnetic layer containing the abrasive includes the dispersing agent described in paragraphs [0012] to [0022] of JP2013-131285A.

The magnetic layer described above can be provided on the surface of the non-magnetic support directly or indirectly through the non-magnetic layer.

Non-Magnetic Layer

Next, the non-magnetic layer will be described. The magnetic tape may have the magnetic layer directly on the surface of the non-magnetic support, or may have the magnetic layer on the surface of the non-magnetic support via the non-magnetic layer containing the non-magnetic powder. The non-magnetic powder used in the non-magnetic layer may be a powder of an inorganic substance or powder of organic substance. In addition, carbon black and the like can be used. Examples of the powder of the inorganic substance include powders of metal, metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide. These non-magnetic powders can be purchased as a commercially available product or can be manufactured by a well-known method. For details thereof, the reference can be made to paragraphs [0146] to [0150] of JP2011-216149A. For carbon black which can be used in the non-magnetic layer, the reference can be made to paragraphs [0040] and [0041] of JP2010-024113A. The content amount (filling percentage) of the non-magnetic powder of the non-magnetic layer is preferably 50 to 90 mass % and more preferably 60 to 90 mass %.

The non-magnetic layer can include the binding agent and can also include the additive. With respect to other details of the binding agent or the additive of the non-magnetic layer, the well-known technique regarding the non-magnetic layer can be applied. In addition, in regards to the type and the content amount of the binding agent, and the type and the content of the additive, for example, the well-known technique regarding the magnetic layer can be applied.

In the present invention and the present specification, the non-magnetic layer also includes a substantially non-magnetic layer including a small amount of ferromagnetic powder as impurities, for example, or intentionally, together with the non-magnetic powder. Here, the substantially non-magnetic layer is a layer having a residual magnetic flux density equal to or smaller than 10 mT, a layer having a coercivity equal to or smaller than 7.96 kA/m (100 Oe), or a layer having a residual magnetic flux density equal to or smaller than 10 mT and a coercivity equal to or smaller than 7.96 kA/m (100 Oe). It is preferable that the non-magnetic layer does not have a residual magnetic flux density and a coercivity.

Back Coating Layer

The magnetic tape may or may not include a back coating layer including non-magnetic powder on a surface side of the non-magnetic support opposite to the surface provided with the magnetic layer. Preferably, the back coating layer contains either one or both of carbon black and inorganic powder. The back coating layer can include the binding agent and can also include the additive. With respect to the binding agent and the additive of the back coating layer, the well-known technique regarding the back coating layer can be applied, and the well-known technique regarding the formulation of the magnetic layer and/or the non-magnetic layer can be applied. For example, for the back coating layer, the reference can be made to paragraphs [0018] to [0020] of JP2006-331625A and page 4, line 65, to page 5, line 38, of U.S. Pat. No. 7,029,774B.

Various Thicknesses

In regards to the thickness (total thickness) of the magnetic tape, it is required to increase the recording capacity (higher capacity) of the magnetic tape with the enormous increase in the amount of information in recent years. As a means for increasing the recording capacity, it is possible to reduce the thickness of the magnetic tape (hereinafter, it is also described as “thinning”.) and increase the length of the magnetic tape accommodated in one roll of the magnetic tape cartridge. From this point of view, the thickness (total thickness) of the magnetic tape is preferably 5.6 μm or less, more preferably 5.5 μm or less, still more preferably 5.4 μm or less, and further more preferably 5.3 μm or less. In addition, from the viewpoint of easy handling, the thickness of the magnetic tape is preferably 3.0 μm or more, more preferably 3.5 μm or more. With respect to the thickness of the magnetic tape, the value of TDStens tends to increase as the thickness decreases.

The thickness (total thickness) of the magnetic tape can be measured by the following method.

Ten tape samples (for example, 5 to 10 cm in length) are cut out from a random part of the magnetic tape, and the tape samples are stacked to measure the thickness. A value (thickness per one tape sample) obtained by dividing the measured thickness by 1/10 is defined as the tape thickness. The thickness measurement can be performed using a known measuring device capable of measuring the thickness on the order of 0.1 μm.

The thickness of the non-magnetic support is preferably 3.0 to 5.0 μm.

The thickness of the magnetic layer can be optimized according to the amount of saturation magnetization of the magnetic head used, a head gap length, a band of a recording signal, and the like, and is generally 0.01 μm to 0.15 μm, preferably 0.02 μm to 0.12 μm and more preferably 0.03 μm to 0.1 μm from the viewpoint of high-density recording. The magnetic layer may be at least a single layer, the magnetic layer may be separated into two or more layers having different magnetic characteristics, and a configuration in regards to a well-known multilayered magnetic layer can be applied as the magnetic layer. A thickness of the magnetic layer in a case where the magnetic layer is separated into two or more layers is defined as a total thickness of the layers.

The thickness of the non-magnetic layer is, for example, 0.1 to 1.5 μm, preferably 0.1 to 1.0 μm.

A thickness of the back coating layer is preferably 0.9 μm or less, and more preferably 0.1 to 0.7 μm.

Various thicknesses such as the thickness of the magnetic layer can be obtained by the following method.

After exposing the cross section in the thickness direction of the magnetic tape with an ion beam, the cross section in the exposed cross section is observed with a scanning electron microscope. Various thicknesses can be obtained as an arithmetic average of thicknesses obtained at two randomly points in cross section observation. Alternatively, the various thicknesses can be obtained as a design thicknesses calculated from manufacturing conditions and the like.

Manufacturing Step

Preparation of Each Layer Forming Composition

Moreover, a step of preparing a composition for forming the magnetic layer, the non-magnetic layer, or the back coating layer can generally include at least a kneading step, a dispersing step, and a mixing step provided before and after these steps as necessary. Each step may be divided into two or more stages. The component used in the preparation of each layer forming composition may be added at an initial stage or in a middle stage of each step. As a solvent, one kind or two or more kinds of various kinds of solvents usually used for manufacturing the coating type magnetic recording medium can be used. With respect to the solvent, for example, the reference can be made to paragraphs paragraph [0153] of JP2011-216149A. In addition, each component may be separately added in two or more steps. For example, a binding agent may be divided and added in a kneading step, a dispersing step, and a mixing step for adjusting viscosity after the dispersion. In order to manufacture the above magnetic tape, known manufacturing techniques can be used in various steps. In the kneading step, it is preferable to use a kneader having a strong kneading force such as an open kneader, a continuous kneader, a pressure kneader, or an extruder. With respect to details of these kneading treatments, the reference can be made to JP1989-106338A (JP-H01-106338A) and JP1989-079274A (JP-H01-079274A). As a dispersing device, a well-known dispersing device can be used. Filtering may be performed by a known method at a random stage of preparing the composition for forming each layer. The filtering can be performed by using a filter, for example. As a filter used in the filtering, a filter having a pore diameter of 0.01 to 3 μm (for example, a filter made of glass fiber or a filter made of polypropylene) can be used, for example.

Coating Step

The magnetic layer can be formed by directly coating the magnetic layer forming composition on the surface of the non-magnetic support or performing multilayer coating of the magnetic layer forming composition with the composition for forming the non-magnetic layer in order or at the same time.

The back coating layer can be formed by coating a composition for forming the back coating layer to the surface of the non-magnetic support opposite to the (alternatively, the non-magnetic layer and/or the magnetic layer are provided in sequence) surface having the non-magnetic layer and/or the magnetic layer. With respect to details of the coating for forming each layer, the reference can be made to a paragraph [0066] of JP2010-231843A.

Other Steps

Known techniques can be applied to other various steps for manufacturing the magnetic tape. With respect to various steps, the reference can be made to paragraphs [0067] to [0070] of JP2010-231843A, for example. For example, a coating layer of the composition for forming the magnetic layer can be subjected to an orientation treatment in an orientation zone while the coating layer is in a wet state. With respect to the orientation treatment, the various well-known techniques such as a description disclosed in a paragraph [0052] of JP2010-024113A can be used. For example, a vertical orientation treatment can be performed by a well-known method such as a method using a polar opposing magnet. In the orientation zone, a drying speed of the coating layer can be controlled depending on a temperature and a flow rate of dry air and/or a transportation speed in the orientation zone. In addition, the coating layer may be preliminarily dried before the transportation to the orientation zone.

By going through various steps, a long magnetic tape raw material can be obtained. The obtained magnetic tape raw material is cut (slit) into a width of the magnetic tape to be wound around the magnetic tape cartridge by a known cutting machine. The width is determined according to the standard and is usually ½ inch. ½ inch=12.65 mm.

A servo pattern is formed on the magnetic tape obtained by slitting. Details of the servo pattern will be described later.

Heat Treatment

In one aspect, the magnetic tape may be a magnetic tape manufactured through the following heat treatment. Performing the following heat treatment can contribute, for example, to reducing the ratio of the change of the TDStens to the change of relative humidity and/or temperature.

As the heat treatment, a magnetic tape cut into a width determined according to a standard by slitting is wound around a core member, and the heat treatment can be performed in a wound state.

In one aspect, the heat treatment is performed in a state in which the magnetic tape is wound around a core member (hereinafter, referred to as a “winding core for the heat treatment”.) for the heat treatment, the magnetic tape after the heat treatment is wound around a reel of the magnetic tape cartridge, and the magnetic tape cartridge in which the magnetic tape is wound around the reel can be manufactured.

The winding core for the heat treatment can be made of metal, resin, paper, or the like. A material of the winding core for the heat treatment is preferably a material having high stiffness from the viewpoint of suppressing the occurrence of winding failures such as spokes. From this point, the winding core for the heat treatment is preferably made of metal or resin. In addition, as an index of stiffness, a bending elastic modulus of the material of the winding core for the heat treatment is preferably 0.2 GPa or more, more preferably 0.3 GPa or more. On the other hand, since high stiffness materials are generally expensive, the use of a winding core for the heat treatment made of a material having a stiffness exceeding a stiffness capable of suppressing the occurrence of the winding failures leads to an increase in cost. Considering the above points, the bending elastic modulus of the material of the winding core for the heat treatment is preferably 250 GPa or less. The bending elastic modulus is a value measured according to an international organization for standardization (ISO) 178, and the bending elastic modulus of various materials is known. In addition, the winding core for the heat treatment may be a solid or hollow core member. In the case of a hollow shape, the wall thickness is preferably 2 mm or more from the viewpoint of maintaining the stiffness. Further, the winding core for the heat treatment may or may not have a flange.

It is preferable that a magnetic tape of longer than a length (hereinafter, referred to as a “final product length”.) to be finally accommodated in the magnetic tape cartridge is prepared as the magnetic tape to be wound around the winding core for the heat treatment, and the heat treatment is performed by placing the magnetic tape under a heat treatment environment while being wound around the winding core for the heat treatment. It is preferable that the length of the magnetic tape wound around the winding core for the heat treatment is equal to or longer than the final product length, and is defined as the “final product length+α” from the viewpoint of easiness of winding around the winding core for the heat treatment and the like. This a is preferably 5 m or more from the viewpoint of easiness of winding. A tension during winding on the winding core for the heat treatment is preferably 0.1 N (newton) or more. In addition, from the viewpoint of suppressing the occurrence of excessive deformation, the tension during winding around the winding core for the heat treatment is preferably 1.5 N or less, more preferably 1.0 N or less. An outer diameter of the winding core for the heat treatment is preferably 20 mm or more, and more preferably 40 mm or more, from the viewpoint of easiness of winding and suppression of coiling (curl in the longitudinal direction). Further, the outer diameter of the winding core for the heat treatment is preferably 100 mm or less, more preferably 90 mm or less. A width of the winding core for the heat treatment may be equal to or larger than a width of the magnetic tape wound around the winding core. In addition, in a case where the magnetic tape is removed from the winding core for the heat treatment after the heat treatment, it is preferable to remove the magnetic tape from the winding core for the heat treatment after the magnetic tape and the winding core for the heat treatment have been sufficiently cooled in order to suppress unintended tape deformation during the removal operation. It is preferable that the removed magnetic tape is once wound on another winding core (referred to as a “winding core for temporary winding”), and then the magnetic tape is wound on the reel (generally, the outer diameter is about 40 to 50 mm.) of the magnetic tape cartridge from the winding core for temporary winding. As a result, the magnetic tape can be wound on the reel of the magnetic tape cartridge while maintaining a relationship between the inner side and the outer side with respect to the winding core for the heat treatment of the magnetic tape during the heat treatment. With respect to the details of the winding core for temporary winding and the tension in a case of winding the magnetic tape around the winding core, the above description regarding the winding core for the heat treatment can be referred to. In an aspect in which the heat treatment is applied to a magnetic tape having a length of “final product length+α”, the length of “+α” may be cut off at a random stage. For example, in one aspect, the magnetic tape for the final product length may be wound from the winding core for temporary winding to the reel of the magnetic tape cartridge, and the remaining “+α” length may be cut off. From the viewpoint of reducing the part to be cut off and discarded, the above α is preferably 20 m or less.

A specific aspect of the heat treatment performed in the state of being wound around the core member as described above will be described below.

An ambient temperature for the heat treatment (hereinafter, referred to as a “heat treatment temperature”) is preferably 40° C. or more, and more preferably 50° C. or more. On the other hand, from the viewpoint of suppressing excessive deformation, the heat treatment temperature is preferably 75° C. or less, more preferably 70° C. or less, and still more preferably 65° C. or less.

A weight absolute humidity of the atmosphere in which the heat treatment is performed is preferably 0.1 g/kg Dryair or more, and more preferably 1 g/kg Dryair or more. An atmosphere having the weight absolute humidity in the above range is preferable since it can be prepared without using a special apparatus for reducing moisture. On the other hand, the weight absolute humidity is preferably 70 g/kg Dryair or less, and more preferably 66 g/kg Dryair or less, from the viewpoint of suppressing reduction in workability due to dew condensation. The heat treatment time is preferably 0.3 hours or more, more preferably 0.5 hours or more. In addition, the heat treatment time is preferably 48 hours or less from the viewpoint of production efficiency.

Formation of Servo Pattern

A “formation of the servo pattern” can also be referred to as “recording a servo signal”. The formation of the servo pattern will be described below.

The servo pattern is usually formed along the longitudinal direction of the magnetic tape. A method of control (servo control) using the servo signal includes timing-based servo (TBS), amplitude servo, frequency servo, and the like.

As shown in an european manufacturers association (ECMA)—319 (June 2001), magnetic tapes (generally called “LTO tape”) conforming to a linear tape—open (LTO) standard employ a timing-based servo method. In the timing-based servo method, the servo pattern is configured by continuously disposing a plurality of pairs of magnetic stripes (also called a “servo stripe”) which are not parallel to each other in the longitudinal direction of the magnetic tape. In the present invention and the present specification, a “timing-based servo pattern” refers to a servo pattern that enables head tracking in the servo system of the timing-based servo method. As described above, the reason why the servo pattern is composed of pairs of magnetic stripes which are not parallel to each other is to teach the servo signal reading element passing on the servo pattern a passing position. Specifically, the pair of magnetic stripes are formed such that an interval thereof continuously changes along the width direction of the magnetic tape, and a relative position between the servo pattern and the servo signal reading element can be known by reading the interval by the servo signal reading element. This relative position information enables tracking of the data track. Therefore, a plurality of servo tracks are usually set on the servo pattern along the width direction of the magnetic tape.

The servo band is configured with the servo pattern continuous in the longitudinal direction of the magnetic tape.

Usually, a plurality of servo bands are provided on the magnetic tape. For example, the number of LTO tapes is five. A region sandwiched between two adjacent servo bands is the data band. The data band is configured with a plurality of data tracks, and each data track corresponds to each servo track.

In addition, in one aspect, as shown in JP2004-318983A, information indicating a servo band number (referred to as “servo band ID (identification)” or “UDIM (Unique Data Band Identification Method) information”) is embedded in each servo band. This servo band ID is recorded by shifting a specific one of the plurality of pairs of the servo stripes in the servo band so that positions thereof are relatively displaced in a longitudinal direction of the magnetic tape. Specifically, a way of shifting the specific one of the plurality of pairs of servo stripes is changed for each servo band. Accordingly, since the recorded servo band ID is unique for each servo band, the servo band can be uniquely specified only by reading one servo band with a servo signal reading element.

It should be noted that as a method for uniquely specifying the servo band, there is a method using a staggered method as shown in ECMA-319 (June 2001). In the staggered method, a group of a plurality of pairs of magnetic stripes that are disposed continuously in the longitudinal direction of the magnetic tape and are not parallel to each other (servo stripes) is recorded so as to be shifted in a longitudinal direction of the magnetic tape for each servo band. Since this combination of shifting methods between adjacent servo bands is unique throughout the magnetic tape, it is possible to uniquely specify the servo band in a case of reading a servo pattern with two servo signal reading elements.

As shown in ECMA-319 (June 2001), information indicating a position of the magnetic tape in the longitudinal direction (also referred to as “Longitudinal Position (LPOS) information”) is usually embedded in each servo band. This LPOS information is also recorded by shifting the positions of the pair of servo stripes in the longitudinal direction of the magnetic tape, as the UDIM information. Here, unlike the UDIM information, in this LPOS information, the same signal is recorded in each servo band.

It is also possible to embed, in the servo band, the other information different from the above UDIM information and LPOS information. In this case, the embedded information may be different for each servo band as the UDIM information or may be common to all servo bands as the LPOS information.

As a method of embedding information in the servo band, it is possible to employ a method other than the above. For example, a predetermined code may be recorded by thinning out a predetermined pair from the group of pairs of servo stripes.

A head for forming the servo pattern is called a servo write head. The servo write head usually has a pair of gaps corresponding to the pair of magnetic stripes as many as the number of servo bands. Usually, a core and a coil are connected to each pair of gaps, and by supplying a current pulse to the coil, a magnetic field generated in the core can cause generation of a leakage magnetic field in the pair of gaps. In a case of forming the servo pattern, by inputting a current pulse while running the magnetic tape on the servo write head, the magnetic pattern corresponding to the pair of gaps is transferred to the magnetic tape to form the servo pattern. A width of each gap can be appropriately set according to a density of the servo pattern to be formed. The width of each gap can be set to, for example, 1 μm or less, 1 to 10 μm, 10 μm or more, and the like.

Before the servo pattern is formed on the magnetic tape, the magnetic tape is usually subjected to a demagnetization (erasing) treatment. This erasing treatment can be performed by applying a uniform magnetic field to the magnetic tape using a direct current magnet or an alternating current magnet. The erasing treatment includes direct current (DC) erasing and alternating current (AC) erasing. AC erasing is performed by gradually decreasing an intensity of the magnetic field while reversing a direction of the magnetic field applied to the magnetic tape. On the other hand, DC erasing is performed by applying a unidirectional magnetic field to the magnetic tape. As the DC erasing, there are two methods. A first method is horizontal DC erasing of applying a magnetic field in unidirection along a longitudinal direction of the magnetic tape. A second method is vertical DC erasing of applying a magnetic field in unidirection along a thickness direction of the magnetic tape. The erasing treatment may be performed on the entire magnetic tape or may be performed for each servo band of the magnetic tape.

A direction of the magnetic field of the servo pattern to be formed is determined according to a direction of the erasing. For example, in a case where the horizontal DC erasing is performed to the magnetic tape, the servo pattern is formed so that the direction of the magnetic field is opposite to the direction of the erasing. Therefore, an output of a servo signal obtained by reading the servo pattern can be increased. It should be noted that As shown in JP2012-053940A, in a case where a magnetic pattern is transferred to, using the gap, a magnetic tape that has been subjected to vertical DC erasing, a servo signal obtained by reading the formed servo pattern has a monopolar pulse shape. On the other hand, in a case where the magnetic pattern is transferred to, using the gap, a magnetic tape that has been subjected to horizontal DC erasing, a servo signal obtained by reading the formed servo pattern has a bipolar pulse shape.

Magnetic Tape Cartridge

One aspect of the present invention relates to a magnetic tape cartridge including the magnetic tape.

Details of the magnetic tape included in the tape cartridge are as described above.

In the magnetic tape cartridge, generally, the magnetic tape is accommodated inside a cartridge main body in a state of being wound around a reel. The reel is rotatably comprised inside the cartridge main body. As the magnetic tape cartridge, a single reel type magnetic tape cartridge having one reel inside the cartridge main body and a dual reel type magnetic tape cartridge having two reels inside the cartridge main body are widely used. In a case where the single reel type magnetic tape cartridge is mounted on a magnetic tape apparatus for recording and/or reproducing data on the magnetic tape, the magnetic tape is pulled out of the magnetic tape cartridge to be wound around the reel on the magnetic tape apparatus side. A magnetic head is disposed in a magnetic tape transportation path from the magnetic tape cartridge to a winding reel. Feeding and winding of the magnetic tape are performed between a reel (supply reel) on the magnetic tape cartridge side and a reel (winding reel) on the magnetic tape apparatus side. During this time, the data is recorded and/or reproduced as the magnetic head and the magnetic layer surface of the magnetic tape come into contact with each other to be slid on each other. On the other hand, in the dual reel type magnetic tape cartridge, both the supply reel and the winding reel are provided inside the magnetic tape cartridge.

The magnetic tape cartridge may include a cartridge memory in one aspect. The cartridge memory can be, for example, a non-volatile memory, and the tension adjustment information is already recorded or tension adjustment information is recorded. The tension adjustment information is information for adjusting the tension applied in the longitudinal direction of the magnetic tape. With respect to the cartridge memory, the description below can be referred to.

The magnetic tape and the magnetic tape cartridge can be suitably used in the magnetic tape apparatus (in other words, a magnetic recording and reproducing system) for controlling the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape.

Magnetic Tape Apparatus

One aspect of the present invention relates to the magnetic tape apparatus including the magnetic tape cartridge. In the magnetic tape apparatus, data can be recorded on the magnetic tape and/or data recorded on the magnetic tape can be reproduced by sliding the surface of the magnetic layer of the magnetic tape in contact with the magnetic head. The magnetic tape apparatus can attachably and detachably include a magnetic tape cartridge according to one aspect of the present invention.

The magnetic tape cartridge can be mounted to the magnetic tape apparatus comprising the magnetic head and used for recording and/or reproducing data. In the present invention and the present specification, the “magnetic tape apparatus” means an apparatus capable of performing at least one of recording data on the magnetic tape and reproducing data recorded on the magnetic tape. Such an apparatus is generally referred to as a drive. The magnetic head included in the magnetic tape apparatus can be the recording head capable of recording data on the magnetic tape, and can also be a reproducing head capable of reproducing data recorded on the magnetic tape. In addition, in one aspect, the magnetic tape apparatus can include both the recording head and the reproducing head as separate magnetic heads. In another aspect, the magnetic head included in the magnetic tape apparatus can have a configuration in which both the recording element and a reproducing element are comprised in one magnetic head.

As the reproducing head, a magnetic head (MR head) including a magneto resistive (MR) element capable of reading information recorded on the magnetic tape with high sensitivity as a reproducing element is preferable. As the MR head, various known MR heads (for example, a giant magneto resistive (GMR) head, a tunnel magneto resistive (TMR) head, and the like) can be used. In addition, the magnetic head that records data and/or reproduces data may include a servo pattern reading element. Alternatively, the magnetic head (servo head) comprising the servo pattern reading element may be included in the magnetic tape apparatus as a head different from the magnetic head that records data and/or reproduces data. For example, the magnetic head (hereinafter, also called a “recording and reproducing head”) that records data and/or reproduces recorded data can include two servo signal reading elements, and each of the two servo signal reading elements can simultaneously read two servo bands adjacent to each other across the data band. One or more data elements can be disposed between the two servo signal reading elements. An element for recording data (recording element) and an element for reproducing data (reproducing element) are collectively referred to as “data element”.

By reproducing data using a reproducing element having a narrow reproduction track width as a reproducing element, data recorded in high-density can be reproduced with high sensitivity. From this viewpoint, the reproduction track width of the reproducing element is preferably 0.8 μm or less. The reproduction track width of the reproducing element can be, for example, 0.3 μm or more. However, it is also preferable to fall below this value from the above viewpoint.

On the other hand, as the reproduction track width becomes narrower, a phenomenon such as defective reproduction due to off-track is more likely to occur. In order to suppress the occurrence of such a phenomenon, it is preferable to use the magnetic tape apparatus that controls the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape.

In a case of recording data and/or reproducing recorded data, first, tracking using the servo signal can be performed. That is, by making the servo signal reading element follow a predetermined servo track, the data element can be controlled so as to pass over the target data track. The movement of the data track is performed by changing the servo track read by the servo signal reading element in the tape width direction.

In addition, the recording and reproducing head can also perform recording and/or reproduction to other data bands. In that case, the servo signal reading element may be moved to a predetermined servo band by using the UDIM information described above, and tracking for the servo band may be started.

FIG. 1 shows a disposition example of the data band and the servo band. In FIG. 1, in the magnetic layer of a magnetic tape MT, a plurality of servo bands 1 are disposed between the guide bands 3. A plurality of regions 2 each of which is sandwiched between two servo bands are data bands. The servo pattern is a magnetization region, and is formed by magnetizing a specific region of the magnetic layer with the servo write head. A region magnetized by the servo write head (a position where the servo pattern is formed) is determined by the standard. For example, in an LTO Ultrium format tape which is based on a local standard, a plurality of servo patterns tilted with respect to a tape width direction as shown in FIG. 2 are formed on a servo band, in a case of manufacturing a magnetic tape. Specifically, in FIG. 2, a servo frame SF on the servo band 1 is configured with a servo sub-frame 1 (SSF1) and a servo sub-frame 2 (SSF2). The servo sub-frame 1 is configured with an A burst (in FIG. 2, reference numeral A) and a B burst (in FIG. 2, reference numeral B). The A burst is configured with servo patterns A1 to A5 and the B burst is configured with servo patterns B1 to B5. Meanwhile, the servo sub-frame 2 is configured with a C burst (in FIG. 2, reference numeral C) and a D burst (in FIG. 2, reference numeral D). The C burst is configured with servo patterns C1 to C4 and the D burst is configured with servo patterns D1 to D4. Such 18 servo patterns are disposed in the sub-frames in the arrangement of 5, 5, 4, 4, as the sets of 5 servo patterns and 4 servo patterns, and are used for identifying the servo frames. FIG. 2 shows one servo frame for illustration. In practice, however, a plurality of servo frames are disposed in each servo band in the running direction in the magnetic layer of the magnetic tape on which the head tracking of the timing-based servo method is performed. In FIG. 2, an arrow shows the running direction. For example, an LTO Ultrium format tape usually has at least 5000 servo frames per meter of tape length in each servo band of the magnetic layer.

The magnetic tape apparatus preferably has a tension adjusting mechanism for controlling the dimension in the width direction of the magnetic tape by adjusting the tension applied in the longitudinal direction of the magnetic tape. An example of such a magnetic tape apparatus will be described below with reference to FIG. 3. However, the present invention is not limited to an example shown in FIG. 3.

Structure of Magnetic Tape Apparatus

A magnetic tape apparatus 10 shown in FIG. 3 controls a recording and reproducing head unit 12 according to an instruction from the control apparatus 11, and records and reproduces data on the magnetic tape MT.

The magnetic tape apparatus 10 has a configuration capable of detecting and adjusting tension applied in the longitudinal direction of the magnetic tape from spindle motors 17A and 17B for controlling rotation of a magnetic tape cartridge reel and a take-up reel and their driving apparatuses 18A and 18B.

The magnetic tape apparatus 10 has a configuration in which a magnetic tape cartridge 13 can be loaded.

The magnetic tape apparatus 10 has a cartridge memory reading and writing apparatus 14 capable of reading and writing the cartridge memory 131 in the magnetic tape cartridge 13.

In a magnetic tape cartridge 13 mounted on the magnetic tape apparatus 10, an end portion or a leader pin of the magnetic tape MT is pulled out by an automatic loading mechanism or manually, and the magnetic layer surface of the magnetic tape MT passes on the recording and reproducing head through guide rollers 15A and 15B in a direction contacting with a recording and reproducing head surface of the recording and reproducing head unit 12, and is wound on the take-up reel 16.

The rotation and torque of a spindle motor 17A and a spindle motor 17B are controlled by a signal from the control apparatus 11, and the magnetic tape MT is run at a random speed and tension. A servo pattern previously formed on the magnetic tape can be used to control the tape speed. A tension detection mechanism may be provided between the magnetic tape cartridge 13 and the take-up reel 16 to detect the tension. The tension may be controlled by using the guide rollers 15A and 15B in addition to the control by the spindle motors 17A and 17B.

The cartridge memory reading and writing apparatus 14 is configured to be able to read and write information in the cartridge memory 131 according to instructions from the control apparatus 11. As a communication method between the cartridge memory reading and writing apparatus 14 and the cartridge memory 131, for example, an international organization for standardization (ISO) 14443 method can be adopted.

The control apparatus 11 includes, for example, a controller, a storage unit, a communication unit, and the like.

The recording and reproducing head unit 12 is composed of, for example, a recording and reproducing head, a servo tracking actuator for adjusting a position of the recording and reproducing head in the track width direction, a recording and reproducing amplifier 19, a connector cable for connecting to the control apparatus 11, and the like. The recording and reproducing head is composed of, for example, the recording element for recording data on the magnetic tape, the reproducing element for reproducing data on the magnetic tape, and the servo signal reading element for reading the servo signal recorded on the magnetic tape. For example, one or more recording elements, reproducing elements, and servo signal reading elements are mounted in one magnetic head. Alternatively, each element may be separately provided in a plurality of magnetic heads according to the running direction of the magnetic tape.

The recording and reproducing head unit 12 is configured to be able to record data on the magnetic tape MT in response to an instruction from the control apparatus 11. In addition, the data recorded on the magnetic tape MT is configured to be able to be reproduced in response to an instruction from the control apparatus 11.

The control apparatus 11 has a mechanism for determining the running position of the magnetic tape from the servo signal read from the servo band in a case where the magnetic tape MT is running, and controlling the servo tracking actuator such that the recording element and/or the reproducing element are positioned at a target traveling position (track position). The control of the track position is performed by feedback control, for example.

The control apparatus 11 has a mechanism for obtaining a servo band interval from servo signals read from two adjacent servo bands in a case where the magnetic tape MT is running. In addition, a mechanism has a mechanism for controlling the tension in the longitudinal direction of the magnetic tape by controlling the torque of the spindle motor 17A and the spindle motor 17B and/or the guide rollers 15A and 15B such that the servo band interval becomes the target value. The control of the tension is performed by feedback control, for example. Further, the control apparatus 11 can store the obtained information on the servo band interval in a storage unit inside the control apparatus 11, a cartridge memory 131, an external connection device, or the like.

EXAMPLES

Hereinafter, one aspect of the present invention will be described based on Examples. Here, the present invention is not limited to the aspects shown in the Examples. Unless otherwise specified, the indications of “parts” and “%” described below indicate “parts by mass” and “mass %”. “eq” is an equivalent and is a unit that cannot be converted into an SI unit.

In addition, the following various steps and operations are performed in an environment of a temperature of 20° C. to 25° C. and a relative humidity of 40% to 60% unless otherwise specified.

In Table 1, “PEN” indicates a polyethylene naphthalate support and “PET” indicates a polyethylene terephthalate support. The moisture content and Young's modulus in Table 1 are values measured by the method described above.

Example 1

(1) Preparation of Alumina Dispersion

100.0 parts of alumina powder (Sumitomo chemical HIT-80) having a brunauer-emmett-teller (BET) specific surface area of 20 m²/g and a gelatinization ratio of about 65% are mixed with 3.0 parts of 2,3-dihydroxynaphthalene (manufactured by Tokyo Chemical Industries Co., Ltd), 31.3 parts of a 32% solution (the solvent is a mixture of methyl ethyl ketone and toluene.) of a polyester polyurethane resin (UR-4800 manufactured by Toyobo Co., Ltd. (amount of polar group: 80 meq/kg)) having an SO₃Na group as a polar group, and 570.0 parts of a mixed solution of methyl ethyl ketone and cyclohexanone 1:1 (mass ratio) as a solvent, and dispersed by a paint shaker for 5 hours in the presence of zirconia beads. After the dispersion, a dispersion liquid and the beads are separated by a mesh to obtain an alumina dispersion.

(2) Formulation of Composition for Forming Magnetic Layer

Magnetic Liquid ferromagnetic powder: 100.0 parts Hexagonal barium ferrite powder having an average particle size (average plate diameter) of 21 nm (“BaFe” in Table 1) SO₃Na group-containing polyurethane resin:  14.0 parts Weight-average molecular weight: 70,000, SO₃Na group: 0.2 meq/g Cyclohexanone: 150.0 parts Methyl ethyl ketone: 150.0 parts Abrasive Liquid Alumina dispersion prepared in (1) above:  6.0 parts Silica sol (protrusion forming agent liquid) Colloidal silica (average particle size: 120 nm):  2.0 parts Methyl ethyl ketone:  1.4 parts Other Components Stearic acid:  2.0 parts Stearic acid amide:  0.2 parts Butyl stearate:  2.0 parts Polyisocyanate (CORONATE (registered trademark)  2.5 parts L manufactured by Tosoh Corporation): Finishing additive solvent Cyclohexanone: 200.0 parts Methyl ethyl ketone: 200.0 parts

(3) Formulation of Composition for Forming Non-Magnetic Layer

Non-magnetic inorganic powder: α-iron oxide 100.0 parts Average particle size (average major axis length): 0.15 μm Average acicular ratio: 7 BET specific surface area: 52 m²/g Carbon black: Average particle size: 20 nm  20.0 parts SO₃Na group-containing polyurethane resin:  18.0 parts Weight-average molecular weight: 70,000, SO₃Na group: 0.2 meq/g Stearic acid:  2.0 parts Stearic acid amide:  0.2 parts Butyl stearate:  2.0 parts Cyclohexanone: 300.0 parts Methyl ethyl ketone: 300.0 parts

(4) Formulation of Composition for Forming Back Coating Layer

Carbon black: 100.0 parts Dibutylphthalate (DBP) oil absorption of 74 cm³/100 g  27.0 parts nitrocellulose: Polyester polyurethane resin containing a sulfonic acid  62.0 parts group and/or a salt thereof: Polyester resin:  4.0 parts Alumina powder (BET specific surface area: 17 m²/g):  0.6 parts Methyl ethyl ketone: 600.0 parts Toluene: 600.0 parts Polyisocyanate (CORONATE (registered trademark) L  15.0 parts manufactured by Tosoh Corporation):

(5) Preparation of Each Layer Forming Composition

The composition for forming the magnetic layer is prepared by the following method.

The above magnetic liquid is prepared by dispersing each component for 24 hours (beads-dispersion) using a batch type vertical sand mill. As dispersion beads, zirconia beads having a bead diameter of 0.5 mm are used. Using the sand mill, the prepared magnetic liquid, the abrasive liquid, and other components (silica sol, other components, and finishing additive solvent) are mixed and beads-dispersed for 5 minutes, and then the treatment (ultrasound dispersion) is performed for 0.5 minutes with a batch type ultrasonic apparatus (20 kHz, 300 W). Then, filtering is performed using a filter having a pore diameter of 0.5 μm to prepare the composition for forming the magnetic layer.

The composition for forming the non-magnetic layer is prepared by the following method. The above components excluding lubricants (stearic acid, stearic acid amide, and butyl stearate) are kneaded and diluted with an open kneader, and then dispersion treatment is performed with a horizontal bead mill disperser. After that, the lubricants (stearic acid, stearic acid amide, and butyl stearate) are added and stirring and mixing are performed by a dissolver stirrer to prepare the composition for forming the non-magnetic layer.

The composition for forming the back coating layer is prepared by the following method. The above components except polyisocyanate are introduced into the dissolver stirrer, stirred at a circumferential speed of 10 μm/sec for 30 minutes, and then dispersion treatment is performed by the horizontal bead mill disperser. Then, polyisocyanate is added, and the mixture is stirred and mixed by the dissolver stirrer to prepare the composition for forming the back coating layer

(6) Method for Manufacturing Magnetic Tape and Magnetic Tape Cartridge

A non-magnetic layer is formed by coating and drying the composition for forming the non-magnetic layer prepared in (5) above on the surface of the biaxially stretched support of the type and thickness shown in Table 1 such that the thickness after drying becomes the thickness shown in Table 1. Next, the composition for forming the magnetic layer prepared in (5) above is coated on the non-magnetic layer such that the thickness after drying becomes the thickness shown in Table 1 to form a coating layer. Thereafter, while the coating layer of the composition for forming the magnetic layer is in an undried state, a magnetic field having a magnetic field intensity of 0.3 T is applied in a direction perpendicular to the surface of the coating layer to perform a vertical orientation treatment, and then the magnetic layer is dried to form the magnetic layer. Thereafter, the back coating layer is formed on the surface of the support opposite to the surface on which the non-magnetic layer and the magnetic layer are formed by coating and drying the composition for forming the back coating layer prepared in (5) above such that the thickness after drying becomes the thickness shown in Table 1.

Thereafter, a surface smoothing treatment (calendar treatment) is performed at a calendar temperature (a surface temperature of a calendar roll) of 100 μm/min speed, 300 kg/cm linear pressure, and 90° C. by using the calendar roll composed of a metal roll.

Then, the long magnetic tape raw material is stored in a heat treatment furnace at an ambient temperature of 70° C. for heat treatment (heat treatment time: 36 hours). After the heat treatment, it is slit into a width of ½ inch to obtain a magnetic tape. By recording the servo signal on the magnetic layer of the obtained magnetic tape by a commercially available servo writer, a magnetic tape having data bands, servo bands, and guide bands disposed according to the linear tape—open (LTO) Ultrium format and having servo patterns (timing-based servo pattern) disposed and shaped according to the LTO Ultrium format on the servo bands is obtained. The servo pattern thus formed is a servo pattern according to the description in japanese industrial standards (JIS) X6175: 2006 and Standard ECMA-319 (June 2001). The total number of servo bands is 5, and the total number of data bands is 4.

The magnetic tape (length 970 m) after forming the servo pattern is wound around the winding core for the heat treatment, and the heat treatment is performed while being wound around the winding core. A resin-made solid core member (outer diameter: 50 mm) having a bending elastic modulus of 0.8 GPa is used as the winding core for the heat treatment, and the tension during winding is set to 0.6 N. The heat treatment is performed at the heat treatment temperature shown in Table 1 for 5 hours. The weight absolute humidity of the heat-treated atmosphere is 10 g/kg Dryair.

After the above heat treatment, the magnetic tape and the winding core for the heat treatment are sufficiently cooled, the magnetic tape is removed from the winding core for the heat treatment, the magnetic tape is wound onto the winding core for temporary winding, and then the magnetic tape of the final product length (960 m) is wound from the winding core for the temporary winding to the reel (reel outer diameter: 44 mm) of the magnetic tape cartridge (LTOUltrium 7 data cartridge), the remaining 10 m is cut off, and a leader tape according to item 9 of Standard european computer manufacturers association (ECMA)-319 (June 2001) Section 3 is joined to a terminal of the cutting side by a splicing tape commercially available. As the winding core for temporary winding, a solid core member made of the same material as the winding core for the heat treatment and having the same outer diameter is used, and the tension during winding is set to 0.6 N.

Therefore, the magnetic tape cartridge of the Example 1 of the single reel type in which the magnetic tape having a length of 960 m is wound on the reel is manufactured.

Examples 2 to 14, Comparative Examples 1 to 10

The magnetic tape cartridge is manufactured in the same manner as in Example 1 except that the items in Table 1 are changed as shown in Table 1.

In the Comparative Example in which “none” is described in the column of the “heat treatment temperature” in Table 1, the heat treatment is not performed while being wound around the winding core for the heat treatment.

Example 15

The magnetic tape cartridge is manufactured in the same manner as in Example 1 except that the hexagonal strontium ferrite powder (“SrFe1” in Table 1) manufactured as follows is used as the ferromagnetic powder.

1707 g of SrCO₃, 687 g of H₃BO₃, 1120 g of Fe₂O₃, 45 g of Al (OH)₃, 24 g of BaCO₃, 13 g of CaCO₃, and 235 g of Nd₂O₃ are weighed and mixed with a mixer to obtain a raw material mixture.

The obtained raw material mixture is melted with a platinum crucible at a melting temperature of 1390° C., and while stirring the melting liquid, a tap hole provided at the bottom of the platinum crucible is heated to tap the melt in a rod shape at about 6 g/sec. A hot water is rolled and rapidly cooled with a water-cooled twin roller to manufacture an amorphous body.

280 g of the manufactured amorphous body is charged into an electric furnace, the temperature is increased to 635° C. (crystallization temperature) at a temperature increasing rate of 3.5° C./minute, and the amorphous body is kept at the same temperature for 5 hours to precipitate (crystallize) hexagonal strontium ferrite particles.

Then, the thus obtained crystallized product containing hexagonal strontium ferrite particles is roughly pulverized in a mortar, 1000 g of zirconia beads having a particle diameter of 1 mm and 800 mL of aqueous acetic acid solution having a concentration of 1% are added to a glass bottle, and dispersion treatment is performed for 3 hours by a paint shaker. Then, the obtained dispersion liquid is separated from the beads and placed in a stainless beaker. The dispersion liquid is allowed to stand at a liquid temperature of 100° C. for 3 hours to perform a dissolution treatment of glass components, and then precipitated with a centrifuge, washed by repeated decantation, and dried in a heating furnace at a furnace temperature of 110° C. for 6 hours to obtain a hexagonal strontium ferrite powder.

The hexagonal strontium ferrite powder thus obtained has an average particle size of 18 nm, an activation volume of 902 nm³, an anisotropy constant Ku of 2.2×10⁵ J/m³, and a mass magnetization σs of 49 A·m²/kg.

12 mg of the sample powder is collected from the hexagonal strontium ferrite powder obtained above, and the sample powder is partially dissolved according to dissolution conditions exemplified above, and the elemental analysis of the obtained filtrate is performed by an ICP analyzer, and the surface layer portion content of neodymium atoms is obtained.

Separately, 12 mg of the sample powder is collected from the hexagonal strontium ferrite powder obtained above, and the sample powder is completely dissolved according to dissolution conditions exemplified above, and the elemental analysis of the obtained filtrate is performed by an ICP analyzer, and the bulk content of neodymium atoms is obtained.

The content (bulk content) of neodymium atoms with respect to 100 at % of iron atoms in the hexagonal strontium ferrite powder obtained above is 2.9 at %. In addition, the surface layer portion content of neodymium atoms is 8.0 at %. The ratio between the surface layer portion content and the bulk content, “surface layer portion content/bulk content” is 2.8, and it is confirmed that neodymium atoms are unevenly distributed in the surface layer of the particles.

The fact that the powder obtained above indicates a hexagonal ferrite crystal structure is confirmed by scanning CuKα rays under the conditions of a voltage of 45 kV and an intensity of 40 mA, and measuring the X-ray diffraction pattern under the following conditions (X-ray diffraction analysis). The powder obtained above indicates a crystal structure of a magnetoplumbite type (M-type) hexagonal ferrite. In addition, the crystal phase detected by X-ray diffraction analysis is a magnetoplumbite type single phase.

PANALTICAL X'PertPro diffractometer, PIXcel detector

Soller slit of incident beam and diffracted beam: 0.017 radians

Fixed angle of dispersion slit: ¼ degree

Mask: 10 mm

Anti-scatter slit: ¼ degree

Measurement mode: continuous

Measurement time per stage: 3 seconds

Measurement speed: 0.017 degrees per second

Measurement step: 0.05 degree

Example 16

The magnetic tape cartridge is manufactured in the same manner as in Example 1 except that the hexagonal strontium ferrite powder (“SrFe2” in Table 1) manufactured as follows is used as the ferromagnetic powder.

1725 g of SrCO₃, 666 g of H₃BO₃, 1332 g of Fe₂O₃, 52 g of Al (OH)₃, 34 g of CaCO₃, and 141 g of BaCO₃ are weighed and mixed in a mixer to obtain a raw material mixture.

The obtained raw material mixture is dissolved with a platinum crucible at a melting temperature of 1380° C., and while stirring the melting liquid, a tap hole provided at the bottom of the platinum crucible is heated to tap the melt in a rod shape at about 6 g/sec. A hot water is rolled and rapidly cooled with a water-cooled twin roller to manufacture an amorphous body.

280 g of the obtained amorphous body is charged into an electric furnace, the temperature is increased to 645° C. (crystallization temperature) at a temperature increasing rate, and the amorphous body is kept at the same temperature for 5 hours to precipitate (crystallize) hexagonal strontium ferrite particles.

Then, the thus obtained crystallized product containing hexagonal strontium ferrite particles is roughly pulverized in a mortar, 1000 g of zirconia beads having a particle diameter of 1 mm and 800 mL of aqueous acetic acid solution having a concentration of 1% are added to a glass bottle, and dispersion treatment is performed for 3 hours by a paint shaker. Then, the obtained dispersion liquid is separated from the beads and placed in a stainless beaker. The dispersion liquid is allowed to stand at a liquid temperature of 100° C. for 3 hours to perform a dissolution treatment of glass components, and then precipitated with a centrifuge, washed by repeated decantation, and dried in a heating furnace at a furnace temperature of 110° C. for 6 hours to obtain a hexagonal strontium ferrite powder.

The hexagonal strontium ferrite powder thus obtained has an average particle size of 19 nm, an activation volume of 1102 nm³, an anisotropy constant Ku of 2.0×10⁵ J/m³, and a mass magnetization σs of 50 A·m²/kg.

Example 17

The magnetic tape cartridge is manufactured in the same manner as in Example 1 except that the ε-iron oxide powder (“ε-iron oxide” in Table 1) manufactured as follows is used as the ferromagnetic powder.

8.3 g of iron (III) nitrate 9 hydrate, 1.3 g of gallium (IT) nitrate 8 hydrate, 190 mg of cobalt (II) nitrate 6 hydrate, 150 mg of titanium (IV) sulfate, and 1.5 g of polyvinylpyrrolidone (PVP) are dissolved in 90 g of pure water. While stirring the solution using a magnetic stirrer, in an air atmosphere, 4.0 g of an aqueous ammonia solution with a concentration of 25% is added under a condition of an ambient temperature of 25° C., and the solution is stirred for 2 hours under the temperature condition of an ambient temperature of 25° C. An aqueous citric acid solution obtained by dissolving 1 g of citric acid in 9 g of pure water is added to the obtained solution, and the solution is stirred for 1 hour. The powder precipitated after stirring is collected by centrifugation, washed with pure water, and dried in a heating furnace having a furnace temperature of 80° C.

800 g of pure water is added to the dried powder, and the powder is dispersed again in water to obtain a dispersion liquid. The temperature of the obtained dispersion liquid is increased to 50° C., and 40 g of the aqueous ammonia solution with a concentration of 25% is added dropwise while stirring. After stirring for 1 hour while maintaining the temperature of 50° C., 14 mL of tetraethoxysilane (TEOS) is added dropwise and stirred for 24 hours. 50 g of ammonium sulfate is added to the obtained reaction solution, the precipitated powder is collected by centrifugation, washed with pure water, and dried in a heating furnace at a furnace temperature of 80° C. for 24 hours to obtain a precursor of the ferromagnetic powder.

The obtained precursor of the ferromagnetic powder is loaded into a heating furnace having a furnace temperature of 1000° C. under an air atmosphere and subjected to a heat treatment for 4 hours.

The precursor of the heat-treated ferromagnetic powder is charged into an aqueous solution of 4 mol/L sodium hydroxide (NaOH), and is stirred for 24 hours while maintaining the liquid temperature at 70° C., whereby the silicate compound, which is impurities, is removed from the precursor of the heat-treated ferromagnetic powder.

Then, the ferromagnetic powder from which the silicate compound is removed is collected by centrifugation and washed with pure water to obtain the ferromagnetic powder.

In a case where the composition of the obtained ferromagnetic powder is confirmed by a high frequency inductively coupled plasma-optical emission spectrometry (ICP-OES), it is Ga, Co, and Ti-substituted ε-iron oxide (ε-Ga_(0.28)Co_(0.05)Ti_(0.05)Fe_(1.62)O₃). In addition, X-ray diffraction analysis is performed under the same conditions as those described in regards to the hexagonal strontium ferrite powder SrFe1, and it is confirmed from the peaks of the X-ray diffraction pattern that the obtained ferromagnetic powder has a crystal structure of a single phase of the ε phase (crystal structure of the ε-iron oxide type), which does not include the crystal structures of the α phase and γ phase.

The ε-iron oxide powder thus obtained has an average particle size of 12 nm, an activation volume of 746 nm³, an anisotropy constant Ku of 1.2×10⁵J/m³, and a mass magnetization σs of 16 A·m²/kg.

The activation volume and anisotropy constant Ku of the hexagonal strontium ferrite powder and the ε-iron oxide powder are values obtained by the method described above using a vibrating sample magnetometer (manufactured by Toei Industry Co., Ltd.) for each ferromagnetic powder.

In addition, the mass magnetization σs is a value measured with a magnetic field intensity of 1194 kA/m (15 kOe) using the vibrating sample magnetometer (manufactured by Toei Industry Co., Ltd.).

Evaluation of Magnetic Tape

(1) Minimum Value of TDStens

TDStens are obtained in five environments (a temperature of 16° C. and relative humidity of 20%, a temperature of 16° C. and relative humidity of 80%, a temperature of 26° C. and relative humidity of 80%, a temperature of 32° C. and relative humidity of 20%, and a temperature of 32° C. and relative humidity of 55) by the following methods.

A magnetic tape cartridge containing the magnetic tape to be measured is placed in the same environment for at least 5 days in order to adapt the magnetic tape cartridge to the measurement environment. Thereafter, in the magnetic tape apparatus shown in FIG. 3 in the measurement environment, the magnetic tape is made to run in a state of applying tension of 0.2 N in the longitudinal direction of the magnetic tape, an interval between two servo bands adjacent to each other across the data band is obtained for each LPOS word, and the servo band interval is obtained as an arithmetic average of the servo band intervals for all LPOS words obtained for the entire servo band intervals in a case where a plurality of servo band intervals exist over the entire range in the longitudinal direction of a tape having a length of 100 m at a random position of the magnetic tape. The interval between two servo bands adjacent to each other across the data band is obtained as follows.

The dimension of the servo pattern is necessary to obtain the distance between two servo bands adjacent to each other across the data band. The dimension standards of the servo pattern depend on the generation of LTO. Therefore, first, an average distance AC between four stripes corresponding to an A burst and a C burst and an azimuth angle α of the servo pattern are measured by using a magnetic force microscope or the like.

Next, the servo patterns formed on the magnetic tape are sequentially read along the tape longitudinal direction by using a reel tester and a servo head comprising two servo signal reading elements (hereinafter, one side is referred to as an upper side and the other side is referred to as a lower side.) fixed at intervals in the direction orthogonal to the longitudinal direction of the magnetic tape. An average time between five stripes corresponding to the A burst and the B burst over the length of 1 LPOS word is defined as a. An average time between four stripes corresponding to the A burst and the C burst over the length of 1 LPOS word is defined as b. At this time, the value defined by AC×(½−a/b)/(2×tan (α)) represents a reading position PES in the width direction based on the servo signal obtained by the servo signal reading element over the length of one LPOS word. The servo pattern reading with respect to 1 LPOS word is performed simultaneously by the two servo signal reading elements on the upper side and the lower side. The PES value obtained by the upper servo signal reading element is defined as PES1 and the PES value obtained by the lower servo signal reading element is defined as PES2. As “PES2-PES1”, the interval between two servo bands adjacent to each other across the data band can be obtained with respect to 1 LPOS word. This is because the upper and lower servo pattern reading elements are fixed to the servo head and their intervals do not change.

From the above, G_(0.2N) is determined.

After measuring G_(0.2N), the tension applied in the longitudinal direction of the magnetic tape is increased to 0.4N, and the servo band interval is measured in the same manner as described above in a state where the tension of 0.4N is applied to obtain G_(0.4N).

After measuring G_(0.4N), the tension applied in the longitudinal direction of the magnetic tape is increased to 0.6N, and the servo band interval is measured in the same manner as described above in a state where the tension of 0.6N is applied to obtain G_(0.6N).

After measuring G_(0.6N), the tension applied in the longitudinal direction of the magnetic tape is increased to 0.8N, and the servo band interval is measured in the same manner as described above in a state where the tension of 0.8N is applied to obtain G_(0.8N).

After measuring G_(0.8N), the tension applied in the longitudinal direction of the magnetic tape is increased to 1.0N, and the servo band interval is measured in the same manner as described above in a state where the tension of 1.0N is applied to obtain G_(1.0N).

After measuring G_(1.0N), the tension applied in the longitudinal direction of the magnetic tape is increased to 1.2N, and the servo band interval is measured in the same manner as described above in a state where the tension of 0.2N is applied to obtain G_(1.2N).

With respect to G_(0.2N), G_(0.4N), G_(0.6N), G_(0.8N), G_(1.0N), and G_(1.2N) obtained by the above method, a slope A obtained by the least-squares method using the servo band intervals obtained in a state where the tension is applied as X of the linear function Y=AX+B (A is a slope, B is an intercept) and Y is defined as the “TDStens” which is the ratio of the change of the servo band interval to the change of tension in the measurement environment.

The above measurement is performed in the above five environments. Thus, the “TDStens” which is the ratio of the change of the servo band interval to the change of tension in the five environments is obtained. Table 1 shows the minimum values of the five TDStens values obtained under each of the five environments.

(2) Ratio of Change of TDStens to Change of Relative Humidity

With respect to the value of five TDStens obtained in the above five environments, TDStens as y of the linear function y=ax+b (a is a slope, b is an intercept), and the slope a obtained by the least-squares method using the relative humidity of the environment in which x is obtained is shown in Table 1 as the ratio of the change of TDStens with respect to the change of relative humidity.

(3) Ratio of Change of TDStens to Change of Temperature

With respect to the value of five TDStens obtained in the above five environments, TDStens as y of the linear function y=cx+d (c is a slope, d is an intercept), and the slope c obtained by the least-squares method using the temperature of the environment in which x is obtained is shown in Table 1 as the ratio of the change of TDStens with respect to the change of temperature.

(4) Tape Thickness

The magnetic tape cartridge after the evaluation in (1) above is placed in an environment having a temperature of 20° C. to 25° C. and a relative humidity of 40% to 60% for 5 days or more to allow the magnetic tape cartridge to adapt to the environment. Then, subsequently, in the same environment, 10 tape samples (length 5 cm) are cut out from a random part of the magnetic tape taken out from the magnetic tape cartridge, and these tape samples are stacked to measure the thickness. The thickness is measured using a Millimar 1240 compact amplifier manufactured by MARH and a digital thickness meter of the Millimar 1301 lead probe. A value (thickness per one tape sample) obtained by dividing the measured thickness by 1/10 is defined as the tape thickness. With respect to each magnetic tape, the tape thickness is the thickness shown in Table 1.

Evaluation of Recording and Reproducing Quality

The recording and reproducing quality is evaluated using the magnetic tape apparatus having the configuration shown in FIG. 3. The recording and reproducing head mounted on the recording and reproducing head unit has a reproducing element (reproduction track width: 0.8 μm) and a recording element of 32 ch or more, and has servo signal recording and reproducing elements on both sides thereof.

Among the above five environments, data is recorded as follows with respect to each of the four environments other than the environment in which TDStens is the minimum value.

The magnetic tape cartridge is placed in the same environment for 5 days or more in order to adapt the magnetic tape cartridge to the measurement environment. Thereafter, the data is recorded in the same environment as follow.

The magnetic tape cartridge is set in the magnetic tape apparatus and the magnetic tape is loaded. Next, while performing servo tracking, the recording and reproducing head unit records pseudo random data having a specific data pattern on the magnetic tape. At that time, the tension in the longitudinal direction of the tape is a constant value. In the data recording, three or more round trips are recorded such that a difference between the values of (PES1+PES2)/2 between adjacent tracks is 1.16 μm. Simultaneously with the recording of the data, the value of the servo band interval of the tape total length is measured every 1 m of the longitudinal position and recorded in the cartridge memory.

The magnetic tape cartridge on which data is recorded as described above is placed in the same environment for 5 days or more in order to adapt the magnetic tape cartridge to the environment in which TDStens is the minimum value. Thereafter, the data is reproduced in the same environment as follow.

The magnetic tape cartridge is set in the magnetic tape apparatus and the magnetic tape is loaded. Then, the data recorded on the magnetic tape are reproduced by the recording and reproducing head unit while performing servo tracking. At that time, the value of the servo band interval is measured simultaneously with reproduction, and the tension applied in the tape longitudinal direction is controlled such that the absolute value of the difference from the servo band interval at the time of recording at the same longitudinal position approaches 0 on the basis of information recorded in the cartridge memory. During reproducing, measurement of the servo band interval and tension control based on it are continuously performed in real time.

In a case where the environment in which the TDStens value is minimum is called “environment E” and the other four environments are called “environment A”, “environment B”, “environment C”, and “environment D”, recording and reproducing are performed in four combinations (recording in environment A and reproducing in environment E, recording in environment B and reproducing in environment E, recording in environment C and reproducing in environment E, recording in environment D and reproducing in environment E). In all combinations, in a case where data of 28 ch or more among 32 ch is correctly read, the recording and reproducing quality is evaluated as “A”, and in other cases, the recording and reproducing quality is evaluated as “B”.

The results described above are shown in Table 1 (Table 1-1 to Table 1-3).

TABLE 1-1 Example Example Example Example Example Example Example Example Example Example 1 2 3 4 5 6 7 8 9 10 Thickness of magnetic 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm layer Thickness of non- 1.0 μm 1.0 μm 0.7 μm 0.7 μm 0.4 μm 0.7 μm 0.4 μm 1.0 μm 1.0 μm 0.7 μm magnetic layer Thickness of non- 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm magnetic support Thickness of back 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm coating layer Thickness of tape 5.6 μm 5.6 μm 5.3 μm 5.3 μm 5.0 μm 5.3 μm 5.0 μm 5.6 μm 5.6 μm 5.3 μm Temperature of heat 50° C. 50° C. 50° C. 60° C. 60° C. 60° C. 60° C. 50° C. 50° C. 50° C. treatment Type of ferromagnetic Bafe Bafe Bafe Bafe Bafe Bafe Bafe Bafe Bafe Bafe powder Type of non-magnetic PET PET PET PET PET PET PET PEN PEN PEN support (A) Young's modulus of 4000 3500 4000 4000 4000 4000 4000 4000 3500 4000 non-magnetic support Width direction (MPa) (B) Young's modulus of 7000 7000 7000 7000 7000 7000 7000 8000 8000 7000 magnetic support Longitudinal direction (MPa) (B) − (A) (MPa) 3000 3500 3000 3000 3000 3000 3000 4000 4500 3000 Moisture content of 0.50% 0.50% 0.50% 0.50% 0.50% 0.20% 0.20% 0.60% 0.60% 0.50% non-magnetic support Minimum value of 1.43 1.72 2.00 1.43 1.86 1.43 1.86 1.43 1.72 2.00 TDStens (μm/N) Ratio of change of 0.020 0.020 0.020 0.017 0.017 0.014 0.014 0.020 0.020 0.020 TDStens to change of temperature (μm/N/° C.) Ratio of change of 0.004 0.004 0.004 0.003 0.003 0.001 0.001 0.004 0.004 0.004 TDStens to change of relative humidity (μm/N/%) Recording and A A A A A A A A A A reproducing quality

TABLE 1-2 Example Example Example Example Example Example Example 11 12 13 14 15 16 17 Thickness of magnetic layer 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm Thickness of non-magnetic layer 0.7 μm 0.4 μm 0.7 μm 0.4 μm 0.7 μm 0.7 μm 0.7 μm Thickness of non-magnetic support 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm Thickness of back coating layer 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm Thickness of tape 5.3 μm 5.0 μm 5.3 μm 5.0 μm 5.3 μm 5.3 μm 5.3 μm Temperature of heat treatment 60° C. 60° C. 60° C. 60° C. 50° C. 50° C. 50° C. Type of ferromagnetic powder BaFe BaFe BaFe BaFe SrFe1 SrFe2 α-iron oxide Type of non-magnetic support PEN PEN PEN PEN PET PET PET (A) Young's modulus of non-magnetic 4000 4000 4000 4000 4000 4000 4000 support Width direction (MPa) (B) Young's modulus of non-magnetic 7000 7000 7000 7000 7000 7000 7000 support Longitudinal direction (MPa) (B) − (A) (MPa) 3000 3000 3000 3000 3000 3000 3000 Moisture content of non-rnagnetic 0.50% 0.50% 0.20% 0.20% 0.50% 0.50% 0.50% support Minimum value of TDStens (μm/N) 1.43 1.86 1.43 1.86 2.00 2.00 2.00 Ratio of change of TDStens to change 0.017 0.017 0.014 0.014 0.020 0.020 0.020 of temperature (μm/N/° C.) Ratio of change of TDStens to change 0.003 0.003 0.001 0.001 0.004 0.004 0.004 of relative humidity (μm/N/%) Recording and reproducing quality A A A A A A A

TABLE 1-3 Comparative Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4 Example 5 Thickness of 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm magnetic layer Thickness of non- 1.0 μm 1.0 μm 1.0 μm 0.7 μm 1.0 μm magnetic layer Thickness of non- 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm magnetic support Thickness of back 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm coating layer Thickness of tape 5.6 μm 5.6 μm 5.6 μm 5.3 μm 5.6 μm Temperature of None None None None 50° C. heat treatment Type of ferromagnetic BaFe BaFe BaFe BaFe BaFe powder Type of non-magnetic PET PET PET PET PET support (A) Young's modulus 7000 6800 5000 5000 7000 of non-magnetic support Width direction (MPa) (B) Young's modulus 4000 4000 6000 6000 4000 of magnetic support Longitudinal direction (MPa) (B) − (A) (MPa) −3000 −2800 1000 1000 −3000 Moisture content of 2.00% 2.00% 2.00% 2.00% 1.00% non-magnetic support Minimum value of 1.14 1.29 1.37 1.57 1.14 TDStens (μm/N) Ratio of change of 0.023 0.023 0.023 0.023 0.014 TDStens to change of temperature (μm/N/° C.) Ratio of change of 0.006 0.006 0.006 0.006 0.003 TDStens to change of relative humidity (μm/N/%) Recording and B B B B B reproducing quality Comparative Comparative Comparative Comparative Comparative Example 6 Example 7 Example 8 Example 9 Example 10 Thickness of 0.1 μm 0.1 μm 0.1 μm 0.1 μm 0.1 μm magnetic layer Thickness of non- 1.0 μm 1.0 μm 1.0 μm 0.7 μm 1.0 μm magnetic layer Thickness of non- 4.0 μm 4.0 μm 4.0 μm 4.0 μm 4.0 μm magnetic support Thickness of back 0.5 μm 0.5 μm 0.5 μm 0.5 μm 0.5 μm coating layer Thickness of tape 5.6 μm 5.6 μm 5.6 μm 5.3 μm 5.6 μm Temperature of None None None None 50° C. heat treatment Type of ferromagnetic BaFe BaFe BaFe BaFe BaFe powder Type of non-magnetic PEN PEN PEN PEN PEN support (A) Young's modulus 8000 7500 5000 5000 8000 of non-magnetic support Width direction (MPa) (B) Young's modulus 4000 4500 6000 6000 4000 of magnetic support Longitudinal direction (MPa) (B) − (A) (MPa) −4000 −3000 1000 1000 −4000 Moisture content of 2.00% 2.00% 2.00% 2.00% 1.00% non-magnetic support Minimum value of 1.14 1.29 1.37 1.57 1.14 TDStens (μm/N) Ratio of change of 0.023 0.023 0.023 0.023 0.014 TDStens to change of temperature (μm/N/° C.) Ratio of change of 0.006 0.006 0.006 0.006 0.003 TDStens to change of relative humidity (μm/N/%) Recording and B B B B B reproducing quality

From the results shown in Table 1, it can be confirmed that the magnetic tape of the Examples is a magnetic tape suitable for use in a magnetic tape apparatus for controlling the dimension in the width direction of the magnetic tape by adjusting the tension applied to the longitudinal direction of the magnetic tape.

One aspect of the present invention is useful in various data storage technical fields. 

What is claimed is:
 1. A magnetic tape comprising: a non-magnetic support and a magnetic layer containing a ferromagnetic powder, wherein the magnetic layer has a plurality of servo bands, and a region sandwiched between two adjacent servo bands is called a data band, among five TDStens measured respectively in the following five environments; a temperature of 16° C. and a relative humidity of 20%, a temperature of 16° C. and a relative humidity of 80%, a temperature of 26° C. and a relative humidity of 80%, a temperature of 32° C. and a relative humidity of 20%, and a temperature of 32° C. and a relative humidity of 55%, a minimum value of the TDStens is 1.43 μm/N or more, where TDStens is a ratio of a change of a servo band interval to a change of a tension obtained from a plurality of servo band intervals measured by respectively applying a plurality of different tensions in a longitudinal direction of a magnetic tape as a value based on a magnetic tape with a ½ inch width and four total data bands, a ratio of a change of the TDStens to a change of the relative humidity, which is obtained from the five TDStens, is 0.005 μm/N/% or less, and a ratio of a change of the TDStens to a change of the temperature, which is obtained from the five TDStens, is 0.020 μm/N/° C. or less.
 2. The magnetic tape according to claim 1, wherein the magnetic tape has a thickness of 5.6 μm or less.
 3. The magnetic tape according to claim 1, wherein the magnetic tape has a thickness of 5.3 μm or less.
 4. The magnetic tape according to any claim 1, wherein the minimum value of the TDStens is 1.43 μm/N or more and 3.00 μm/N or less.
 5. The magnetic tape according to claim 1, wherein a non-magnetic layer containing a non-magnetic powder is provided between the non-magnetic support and the magnetic layer.
 6. The magnetic tape according to claim 1, wherein a back coating layer containing a non-magnetic powder is provided on a surface side of the non-magnetic support opposite to a surface side having the magnetic layer.
 7. The magnetic tape according to any claim 1, wherein the non-magnetic support is an aromatic polyester support.
 8. The magnetic tape according to claim 7, wherein the aromatic polyester support is a polyethylene terephthalate support.
 9. The magnetic tape according to claim 7, wherein the aromatic polyester support is a polyethylene naphthalate support.
 10. A magnetic tape cartridge, comprising a magnetic tape, wherein the magnetic tape comprises a non-magnetic support and a magnetic layer containing a ferromagnetic powder, the magnetic layer has a plurality of servo bands, and a region sandwiched between two adjacent servo bands is called a data band, among five TDStens measured respectively in the following five environments; a temperature of 16° C. and a relative humidity of 20%, a temperature of 16° C. and a relative humidity of 80%, a temperature of 26° C. and a relative humidity of 80%, a temperature of 32° C. and a relative humidity of 20%, and a temperature of 32° C. and a relative humidity of 55%, a minimum value of the TDStens is 1.43 μm/N or more, where TDStens is a ratio of a change of a servo band interval to a change of a tension obtained from a plurality of servo band intervals measured by respectively applying a plurality of different tensions in a longitudinal direction of a magnetic tape as a value based on a magnetic tape with a ½ inch width and four total data bands, a ratio of a change of the TDStens to a change of the relative humidity, which is obtained from the five TDStens, is 0.005 μm/N/% or less, and a ratio of a change of the TDStens to a change of the temperature, which is obtained from the five TDStens, is 0.020 μm/N/° C. or less.
 11. The magnetic tape cartridge according to claim 10, wherein the magnetic tape has a thickness of 5.6 μm or less.
 12. The magnetic tape cartridge according to claim 10, wherein the magnetic tape has a thickness of 5.3 μm or less.
 13. The magnetic tape cartridge according to any claim 10, wherein the minimum value of the TDStens is 1.43 μm/N or more and 3.00 μm/N or less.
 14. The magnetic tape cartridge according to any claim 10, wherein the non-magnetic support is an aromatic polyester support.
 15. A magnetic tape apparatus, comprising a magnetic tape cartridge, wherein the magnetic tape cartridge comprises a magnetic tape, the magnetic tape comprises a non-magnetic support and a magnetic layer containing a ferromagnetic powder, and the magnetic layer has a plurality of servo bands, and a region sandwiched between two adjacent servo bands is called a data band, among five TDStens measured respectively in the following five environments; a temperature of 16° C. and a relative humidity of 20%, a temperature of 16° C. and a relative humidity of 80%, a temperature of 26° C. and a relative humidity of 80%, a temperature of 32° C. and a relative humidity of 20%, and a temperature of 32° C. and a relative humidity of 55%, a minimum value of the TDStens is 1.43 μm/N or more, where TDStens is a ratio of a change of a servo band interval to a change of a tension obtained from a plurality of servo band intervals measured by respectively applying a plurality of different tensions in a longitudinal direction of a magnetic tape as a value based on a magnetic tape with a ½ inch width and four total data bands, a ratio of a change of the TDStens to a change of the relative humidity, which is obtained from the five TDStens, is 0.005 μm/N/% or less, and a ratio of a change of the TDStens to a change of the temperature, which is obtained from the five TDStens, is 0.020 μm/N/° C. or less.
 16. The magnetic tape apparatus according to claim 15, wherein the magnetic tape has a thickness of 5.6 μm or less.
 17. The magnetic tape apparatus according to claim 15, wherein the magnetic tape has a thickness of 5.3 μm or less.
 18. The magnetic tape apparatus according to any claim 15, wherein the minimum value of the TDStens is 1.43 μm/N or more and 3.00 μm/N or less.
 19. The magnetic tape apparatus according to any claim 15, wherein the non-magnetic support is an aromatic polyester support. 